Abstract:As an eco-friendly thermoelectric material, Cu2SnSe3 has recently drawn much attention. However, its high electrical resistivity ρ and low thermopower S prohibit its thermoelectric performance. Herein, we show that a widened band gap and the increased density of states are achieved via S alloying, resulting in 1.6 times enhancement of S (from 170 to 277 μV/K). Moreover, doping In at the Sn site can cause a 19-fold decrease of ρ and a 2.2 times enhancement of S (at room temperature) due to both multivalence bands' participation in electrical transport and the further enhancement of the density of states effective mass, which allows a sharp increase in the power factor. As a result, PF = 9.3 μW cm–1 K–2 was achieved at ∼800 K for the Cu2Sn0.82In0.18Se2.7S0.3 sample. Besides, as large as 44% reduction of lattice thermal conductivity is obtained via intensified phonon scattering by In-doping-induced formation of multidimensional defects, such as Sn vacancies, dislocations, twin boundaries, and CuInSe2 nanoprecipitates. Consequently, a record high figure of merit of ZT = 1.51 at 858 K is acquired for Cu2Sn0.82In0.18Se2.7S0.3, which is 4.7-fold larger than that of pristine Cu2SnSe3.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c03120?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c03120</a>.Temperature dependence of Cp for Cu2SnSe3, Cu2SnSe2.7S0.3, and Cu2Sn0.82In0.18Se2.7S0.3; phase characterization for all investigated samples; temperature dependence of the ZT value for Cu2SnSe3–xSx and the repeatability of thermoelectric performance for Cu2Sn0.82In0.18Se2.7S0.3; calculation details of md*; optical band gaps for S-alloyed Cu2SnSe3; unfolded effective band structure of Cu2SnSe3; calculation of lattice thermal conductivity via the Debye–Callaway model; and the calculation details of thermopower-dependent thermoelectric properties (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c03120/suppl_file/nn1c03120_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Defect Engineering Boosted Ultrahigh Thermoelectric Power Conversion Efficiency in Polycrystalline SnSe

Defect Engineering in Solution-Processed Polycrystalline SnSe Leads to High Thermoelectric Performance

Achieving High Thermoelectric Figure of Merit in Polycrystalline SnSe Via Introducing Sn Vacancies

Enhancement of Thermoelectric Performance of Layered SnSe2 by Synergistic Modulation of Carrier Concentration and Suppression of Lattice Thermal Conductivity

Achieving high thermoelectric performance with Pb and Zn codoped polycrystalline SnSe via phase separation and nanostructuring strategies

Polycrystalline SnSe with a thermoelectric figure of merit greater than the single crystal

Lattice Strain Leads to High Thermoelectric Performance in Polycrystalline SnSe

Realizing High Thermoelectric Performance in p-Type SnSe Crystals via Convergence of Multiple Electronic Valence Bands

Lattice plainification advances highly effective SnSe crystalline thermoelectrics

High thermoelectric properties realized in polycrystalline (Ag, Ga) Co-doped SnSe via two-steps point defects modulation

Polycrystalline SnSe–Sn1–vS Solid Solutions: Vacancy Engineering and Nanostructuring Leading to High Thermoelectric Performance

Defects controlled hole doping and multivalley transport in SnSe single crystals

Recent Advances in Ultrahigh Thermoelectric Performance Material SnSe

Realization of High Thermoelectric Performance in Polycrystalline Tin Selenide through Schottky Vacancies and Endotaxial Nanostructuring

Engineering atomic-level crystal lattice and electronic band structure for extraordinarily high average thermoelectric figure of merit in n-type PbSe

Cold Sintering Mediated Engineering of Polycrystalline SnSe with High Thermoelectric Efficiency

Boosting Thermoelectric Performance of Cu 2 SnSe 3 via Comprehensive Band Structure Regulation and Intensified Phonon Scattering by Multidimensional Defects

Thermoelectric Performance Enhancement in SnS Polycrystals Owing to Hole Doping Combined with Textured Microstructures

Argon Plasma Bombardment Induces Surface‐Rich Sn Vacancy Defects to Enhance the Thermoelectric Performance of Polycrystalline SnSe

A Solvothermal Synthetic Environmental Design for High‐Performance SnSe‐Based Thermoelectric Materials

Realizing High Figure of Merit in Phase-Separated Polycrystalline Sn1-Xpbxse