Abstract:Objectives: The objective of this study was to define the impact of heating rate on the crystal growth, the mechanical properties, and the biocompatibility of three different kinds of CAD/CAM glass-ceramics treated with a conventional furnace. Methods: Lithium disilicate (IPS EMax-CAD, Ivoclar Vivadent) (LS2) and two zirconia reinforced lithium silicate (ZLS) ceramics (Vita Suprinity PC, VITA Zahnfabrik; Celtra Duo, Dentsply Sirona) (ZLSS; ZLSC) were used. The mechanical properties and the crystal growth were evaluated on 42 specimens (n = 14 per group). The thermal treatments recommended by the manufacturers were carried out. All groups were tested for fracture toughness (Ft) and Vickers hardness (Hv). Scanning electron microscope (SEM) images were taken after a slight surface etching with hydrofluoric acid solution (1% for 20 s). Differential Thermal Analysis (DTA) was performed and cellular adhesion with human periodontal ligament stem cells (hPDLSCs) culture was qualitatively assayed. Data were analyzed with Repeated Measurements ANOVA and ANOVA followed by Tukey post hoc test. Results: The crystals' mean size (±SD) after heat treatment was 1650.0 (±340.0) nm for LS2, 854.5 (±155.0) nm for ZLSS and 759.9 (±118.4) nm for ZLSC (p < 0.05 among the groups). As consequence of crystallization, the Hv was 6.1 ± 0.3 GPa for LS2, 7.6 ± 0.7 GPa for ZLSS and 7.1 ± 0.5 GPa for ZLSC (p < 0.05 for LS2 vs ZLSS and ZLSC), while the Ft was 2.2 ± 0.1 MPa m1/2 for LS2, 4.7 ± 0.8 MPa m1/2 for ZLSS and 3.8 ± 0.6 MPa m1/2 for ZLSC (p < 0.05 among the groups). The DTA curves showed a crystallization process for LS2, ZLSS and ZLSC at a temperature range 810-840 °C. The amount of adherent hPDLSCs was superior on LS2 than on ZLS. Conclusions: All the CAD/CAM materials can be properly crystallized if heat treated following the manufacturers' instructions. The crystallization process highly depends on temperature. ZLS glass ceramics show significantly inferior crystals dimensions and higher fracture toughness and Vickers hardness than LS2 ceramic. hPDLSCs cultured on LS2 have a superior adhesion than those cultured on ZLS. Clinical significance: The value of this study relies on the demonstration that a proper heat-treatment of CAD/CAM lithium disilicate and ZLS glass ceramics generates products that are suitable for clinical use . The differences highlightable in mechanical properties and biocompatibility behavior do not affect their successful clinical application.

Effect of simulated gastric acid exposure on the hardness, topographic, and colorimetric properties of machinable and pressable zirconia-reinforced lithium silicate glass-ceramics

Influence of Restoration Thickness and Resin Cement on Translucency and Color of Different Types of Monolithic Zirconia and Lithium Disilicate Ceramic

Gastric acid challenge of lithium disilicate-reinforced glass-ceramics and zirconia-reinforced lithium silicate glass-ceramic after polishing and glazing-impact on surface properties

Staining and bleaching susceptibility of zirconia-reinforced lithium silicate glass-ceramics with different thicknesses, translucencies, and fabrication methods

Impact of Gastric Acid Induced Surface Changes on Mechanical Behavior and Optical Characteristics of Dental Ceramics

Impact of various aging treatments on the microhardness and surface roughness of CAD‐CAM monolithic restorative materials

Surface Roughness Examination of Glass Ionomer Restorative Cements Treated with Acidic and Basic Pediatric Medications: An In Vitro Study

Effect of mouth rinses on the stainability of monolithic lithium disilicate glass-ceramics with different surface treatments: An in vitro study

Effect of gastric acids on the mechanical properties of conventional and CAD/CAM resin composites - an in-vitro study

Evaluation of Color and Translucency of Stained and Glazed Monolithic Lithium Disilicates and Zirconia After Toothbrushing with Different Dentifrices and Thermocycling

Impact of common social habits on optical properties of lithium disilicate glass ceramic crowns: An in vitro study

The Surface Deterioration of Prefabricated Zirconia Crowns on Exposure to Acidulated Phosphate Fluoride Gel: An In Vitro Study

Effect of thermomechanical loading on fracture resistance and failure mode of new pressable zirconia-reinforced lithium disilicate onlay restoration

Effect of Low-Temperature Degradation, Ph-Cycling and Simulated Tooth Brushing on Surface Roughness, Topography, and Polish Retention of Yttrium-Stabilized Tetragonal Zirconia

INFLUENCE OF AGING, BEVERAGES, AND MOUTH WASH SOLUTIONS ON THE MICROSTRUCTURAL AND COLOR STABILITY OF DIFFERENT DENTAL CERAMICS: AN IN VITRO STUDY

Effect of Common Staining Beverages on Color Stability of Polymer-infiltrated Ceramics and Extra Translucent Zirconia: An In Vitro Study

Effect of artificial aging on optical properties of ultra-translucent zirconia ceramics of different brands

Lithium disilicate and zirconia reinforced lithium silicate glass-ceramics for CAD/CAM dental restorations: biocompatibility, mechanical and microstructural properties after crystallization

Translucency and mechanical behavior of partially stabilized monolithic zirconia after staining, finishing procedures and artificial aging

Effect of accelerated aging on dental zirconia-based materials

Effect of sintering procedures on optical properties, chemical composition, and grain size of monolithic zirconia ceramic at different thicknesses after hydrothermal aging: An in vitro study