Synthesis and properties of strontium-doped yttrium manganite

Bo Fu,Wayne Huebner,Mladen F. Trubelja,Vladimir S. Stubican

DOI: https://doi.org/10.1557/jmr.1994.2645

IF: 2.7

1994-10-01

Journal of Materials Research

Abstract:The system Y 1−x Sr x MnO 3 (x = 0.000, 0.005, 0.010, 0.050, and 0.100) was studied as a potential cathode material for solid oxide fuel cells. Powders were prepared using an organometallic precursor; however, achieving homogeneous compositions was complicated due to the presence of intermediate, metastable phases. The desired hexagonal Y 1−x Sr x MnO 3 phase formed from the precursor at 800 °C, while small amounts of a metastable orthorhombic (Y,Sr)MnO 3 phase formed in the temperature range between 850°and 960 °C, and another orthorhombic YMn 2 O 5 phase between 840°and 1200 °C. The metastable (Y, Sr)MnO 3 phase readily transformed into the stable hexagonal phase at about 960 °C. The other metastable intermediate phase, YMn 2 O 5 , was formed as a decomposition product of a portion of the major hexagonal YMnO 3 at 840 °C, and subsequently reacted with Y 2 O 3 back to the hexagonal YMnO 3 at 1200 °C. For the studied compositions, densities higher than 95% theoretical could be obtained by sintering in air at temperatures above 1400 °C for 2 h. The investigated system was comparable in electrical conductivity with the current cathode material La 1−x Sr x MnO 3 , and had an average apparent thermal expansion coefficient between 5 and 7 ppm/°C in the temperature range between 200°and 1000 °C. Unfortunately microcracking was observed in all sintered specimens, possibly caused by a high-temperature phase transition between the hexagonal and cubic polymorphs of Y 1−x Sr x MnO 3 . The microcracking presents a major obstacle to the use of this material as a cathode in solid oxide fuel cells.

materials science, multidisciplinary