Investigation of structural, electrical and electrochemical properties of La0.8Sr0.2Mn1−xScxO3−δ as cathode on yttria-stabilized zirconia electrolyte for intermediate temperature solid oxide fuel cell fabricated by one step dry pressing method
Gayatri Dash,Ela Rout
DOI: https://doi.org/10.1007/s10854-024-12224-0
2024-03-03
Journal of Materials Science Materials in Electronics
Abstract:La 0.8 Sr 0.2 Mn 1− x Sc x O 3− δ perovskite oxides ( x = 0.00, 0.05, 0.10, 0.15) were systematically examined as cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFCs). This study encompassed structural attributes, temperature-dependent weight variations, the electrical conductivity of La 0.8 Sr 0.2 Mn 1− x Sc x O 3−δ compositions, and the single-cell electrochemical performance of La 0.8 Sr 0.2 Mn 1− x Sc x O 3− δ on yttria-stabilized zirconia (YSZ). Further characterizations were carried out through powder X-ray diffraction (XRD), thermogravimetric analysis, DC four-probe method, and impedance spectroscopy, respectively. The X-ray diffraction (XRD) analysis revealed a clear correlation between the increase in Sc 3+ content at the B-site and an increase in both the lattice parameter and lattice volume. The electrical conductivity of La 0.8 Sr 0.2 Mn 1− x Sc x O 3− δ compounds at 750 °C were found to be 137.941, 198.07, 119.789, and 61.036 S cm −1 for x = 0.00, x = 0.05, x = 0.10, and x = 0.15, respectively. When combined with YSZ in a single cell, the area-specific resistances for La 0.8 Sr 0.2 Mn 1− x Sc x O 3− δ were varied between 0.56 and 2.2 Ω cm 2 . La 0.8 Sr 0.2 Mn 0.95 Sc 0.05 O 3−δ exhibited enhanced electrocatalytic activity, with an exchange current density of 39.35 mA cm −2 at 750 °C suggesting the composition as a potential candidate for cathode material in IT-SOFC.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied