Abstract:The wettabilities of molten metals on ceramics are poor normally. In order to improve the wettability, all existing ceramic brazing methods introduce a compound transition layer that is formed by the reaction of active metal and ceramic. The transition layer between brazing seam and ceramic however creates negative effect on the properties of brazing joints. This paper reports our study of the wetting effect of sputtered Al particles on AlN, which enables the direct brazing of AlN using deposited Al-based films as fillers, thereby eliminating the need of a transition layer. The results show that under the bombardment of energetic sputtered Al particles, Al-N chemical bonding is formed at the interface between Al film and AlN, which typically requires temperatures above 850 ℃, much higher than the melting point of Al. The bonding remained intact even after the Al film has been melted, achieving the wetting effect on AlN. As a result, the direct brazing of AlN without the need of a transition layer becomes feasible. The shear strength of Al/AlN joint using this process reaches 104 MPa. The addition of 3.8 at.% Cu to film fillers increases the shear strength to 165 MPa. The fracture is generated in metallic brazing seam in both cases. When Cu content increases to 9.1 at.%, the segregation of Cu at the interface between the brazing seam and the ceramic reduces the shear strength of the joint to 95 MPa. With Al-20 at.% Ge, the brazing temperature can be lowered to 510 ℃, although the segregation of Ge at interface results in a low shear strength of 48 MPa. Instead of the traditional use of molten metals, utilization of the metallic vapor particles to bombard AlN achieves the wetting and the direct brazing of ceramics, with no negative effect of transition layers. This breakthrough method provides a brand new perspective to the technique of ceramic brazing.

Sonocapillary and wetting mechanism during ultrasonic brazing porous Si3N4 ceramics in air

Fast low-temperature ultrasonically soldering porous Si3N4 ceramics in the air

Fabricating porous Si3N4 ceramics joint by ultrasonic brazing at 450 °C

Interfacial Structure and Formation Mechanism of Ultrasonic-Assisted Brazed Joint of Sic Ceramics with Al-12si Filler Metals in Air

Low temperature bonding mechanism of porous Si3N4 ceramics by Sn9Zn solder in ultrasonic-assisted soldering

Brazing SiC ceramic to Zircaloy-4 using Zr-Ni filler alloy: Microstructure, mechanical properties and irradiation behavior

Ultrasonic-assisted wetting and soldering of AlN ceramic by using a nonactive solder (Sn9Zn) in air

Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

Process method of Si3N4 ceramic brazing sealed cavity for high-temperature application

Wetting and brazing of Cf/C composites with Si–Zr eutectic alloys: The formation of nano- and coarse-SiC reaction layers

Bonding mechanism in ultrasonic-assisted soldering of ZrO2 and 304 stainless steel using a micro-alloyed active solder alloy

Realizing the air brazing of ZrO2 ceramics through Al metal

"Wetting" and Brazing of Aln by Sputtered Al

Microstructure and properties of different carbon fiber reinforced ceramic composites brazed joint by Si-Ti alloy filler

Microstructure and formation mechanism of Al2O3/Zn5Al/2024Al joint by ultrasonic assisted soldering process

Joints in Si_3N_4 Ceramics Bonded Using Solid-Liquid State Bonding with Intermetallic Compounds Formed in Situ

Wettability and interfacial reaction mechanism between Ag–Cu alloy and Si3N4 ceramics in air atmosphere

Low-temperature metallization of SiC ceramic with Sn0.5Zn via ultrasound assisted formation of an amorphous transition layer

Pressure brazing of Si3N4 ceramics with Al-Li alloy and high temperature properties of the joints

Ultrasonic effect mechanism on transient liquid phase bonding joints of SiCp reinforced Mg metal matrix composites using Zn-Al-Zn multi-interlayer.

Joining of SiC using CoFeCrNiCuTi high entropy alloy filler by electric current field assisted sintering