Driving the Interfacial Ion-Transfer Kinetics by Mesoporous TiO 2 Spheres for High-Performance Aqueous Zn-Ion Batteries

Xiangyang Zhou,Penghui Cao,Anran Wei,Aiting Zou,Han Ye,Weiping Liu,Jingjing Tang,Juan Yang

DOI: https://doi.org/10.1021/acsami.0c18433

2021-02-09

Abstract:The aqueous zinc-ion batteries (ZIBs) have been considered as a promising energy storage device. However, the ion transfer at the Zn metal anode–electrolyte interface is limited by the sluggish kinetics resulting in high interface resistance. Herein, mesoporous TiO₂ (m-TiO₂) is coated on the Zn foil (Zn-TiO₂) driving the ion's faster transfer to reduce interface resistance (70.1 Ω vs 799.3 Ω of bare Zn). The lower interface resistance is ascribed to shortening the ion transfer path provided by the mesoporous structure and the smaller Zn²⁺ absorption energy barrier of the surface of the Zn-TiO₂ anode as well as the unobstructed ion transfer path at the crystal planes (100) of TiO₂, which have been supported by the density functional theory (DFT) calculation and experiments. Therefore, the Zn-TiO₂ anodes in the symmetrical cells display a low voltage hysteresis (36.5 mV) and long-term cycling stability (500 h at 4.4 mA cm^–2). Especially, the Zn-TiO₂/MnO₂ full cells show superior cycling performance with a high capacity of 269.8 mAh g^–1 after 50 cycles at 0.2 A g^–1 and 210.9 mAh g^–1 after 1000 cycles at 0.5 A g^–1. The analysis of ion-transfer kinetics at the interface provides deep enlightenment and reference for the study of the metal anodes.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18433?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18433</a>.The SEM image of the Zn-20TiO₂ surface; cross-section SEM images and galvanostatic cycling curves; galvanostatic cycling performance of symmetric cells; partial enlarged galvanostatic cycling curves of symmetrical cells; the SEM images and surface pictures; nucleation overpotential; the contact angle; calculation models of Zn absorbed on the surfaces; the XPS spectrum; the XRD results; the TEM results; nitrogen adsorption/desorption isotherms; the XRD patterns of MnO₂; the discharge/charge curves; the long cycling performance at 1 A g^–1; the SEM image of TiO₂ after cycling; the TEM image of m-TiO₂ after cycling; the cycling performance using a 2 M ZnSO₄ electrolyte; the images of the separator; the linear relationships between Zre and ω^–0.5; GITT and diffusion coefficient curves of full cells; cyclic voltammetry curves; SEM images of the electrode after cycling; comparison of cycling performance in the symmetrical cell; and comparison of charge transfer impedance in the symmetrical cell (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18433/suppl_file/am0c18433_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology