Abstract:We present a new simulation-guided process to create nanoporous materials, which does not require specific chemical treatment and solely relies on mechanical deformation of pure highly entangled homopolymer films. Starting from fully equilibrated freestanding thick polymer melt films, we apply a simple "biaxial expansion" deformation. Upon expansion holes form, which are prevented from growing and coalescing beyond a characteristic size due to the entanglement structure of the melt. We investigate the local morphology, the void formation upon expansion, and their stabilization. The dependence of the average void (pore) size and void fraction (porosity) on the total strain and subsequent relaxation is investigated. Furthermore, the stabilization of the porous structure of the thin expanded films through cooling below the glass transition temperature <i>T</i><sub>g</sub> is discussed.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to prepare nanoporous polymer films by mechanical deformation methods without relying on specific chemical treatments. Specifically, the researchers proposed a new simulation - guided process, using the mechanical deformation of pure highly - entangled homopolymer films to create nanoporous materials. The key to this method lies in the formation of pores in the film through biaxial tensile deformation, and the growth and coalescence of these pores are restricted by the entangled structure in the melt, thus remaining within a specific size range.
### Background and Objectives of the Paper
**Background**:
- Nanoporous polymer films have attracted attention due to their wide application potential, such as support media in tissue engineering, separation processes, advanced water treatment, gas separation, medical or food technology, etc.
- Traditional methods for preparing nanoporous films usually rely on the incompatibility of different components. For example, block copolymers are used to design nanostructured materials by adjusting molecular weight, block volume fraction, thermodynamic incompatibility and solvent quality.
- These methods are usually more complex and require precise chemical processes and detailed process control.
**Objectives**:
- Propose a simple method to prepare nanoporous polymer films by mechanical deformation (biaxial stretching) without any additives.
- Use the entangled structure of long chains in the polymer melt as a feature, rather than regarding it as a source of processing difficulties.
- Through rapid mechanical deformation (biaxial stretching), prevent the pores from growing without limit, so as to obtain porous materials with nano - scale pores.
- Stabilize the porous structure below the glass transition temperature by cooling to maintain the porous structure of the material.
### Experimental Methods
**Simulation Setup**:
- Molecular dynamics simulations were carried out using the semi - rigid bead - spring model.
- The simulation started from a fully equilibrated thick free - standing polymer melt film with a film thickness of approximately \(h\approx130\sigma\), containing \(N_c = 1000\) chains, each consisting of \(N = 2000\) monomers.
- Biaxial tensile deformation was applied with a maximum expansion ratio of 4×4, and the film thickness could be freely adjusted.
**Deformation Process**:
- The film was subjected to equi - biaxial strain in two lateral dimensions, and the strain rate \(C\) was selected as 24 to ensure the equilibrium of local monomer packing and avoid chain breakage.
- Comparative experiments between rapid deformation (initial \(C = 32,000\)) and slow deformation (final \(C = 24\)) showed that slow deformation could better maintain the morphology of the pores.
### Results and Discussion
**Morphological Characteristics**:
- The formation of initial pores was observed during the slow deformation process, while mainly density changes were exhibited during the rapid deformation process.
- The formation and growth of pores are restricted by the entangled structure, and the pore size remains at the nano - scale.
- The film thickness reaches a plateau value after expansion, and the size and distribution of pores can be regulated by the strain rate and strain amount.
**Porosity and Pore Size Distribution**:
- The porosity \(\phi\) and pore size distribution \(P(D_{\text{pore}})\) were estimated by Monte Carlo simulation.
- The porosity increases monotonically with the increase of strain. For small deformations (\(\lambda < 2.3\)), the porosity is independent of the strain rate; beyond \(\lambda = 2.3\), rapid deformation leads to a faster increase in porosity.
- The pores formed by slow deformation are larger, while the pores formed by rapid deformation are smaller but more numerous.
**Scattering Function**:
- The scattering function of the expanded film provides additional insights into the structural characteristics and can be directly compared with the experimental results.
- The scattering function \(S_{\parallel}(q_{\parallel})\) parallel to the expansion direction increases with strain at large and medium length scales, while remaining unchanged at short length scales, indicating that the local monomer packing is preserved.
- The scattering function \(S_{\perp}(q_{\perp})\) perpendicular to the film surface can be used to measure the apparent thickness of the film.
**Relaxation Behavior after Deformation**:
- After deformation, the film is at a high temperature (\(T = 1.0\epsilon/k_B\))