Viscoelastic Study of Single Chain Cyclized Polymeric Nanoparticles and Linear Polymers Blends

Si-rong Li,Lin-ru Guo,Yong-sheng Gao,De-zhong Zhou,Wen-xin Wang

DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16304

2017-01-01

Acta Polymerica Sinica

Abstract:It is of great importance to polymerize multivinyl monomers and simultaneously circumvent uncontrollable polymerization process and low gel point. Hereby, a type of divinyl monomer: ethylene glycol dimethacrylate (EGDMA) was successfully homopolymerized by kinetically controlled Cu-0 and Cu-II-meadiated reversible-deactivation radical polymerization (RDRP). The kinetic study showed a well-controlled polymerization behaviour. During the initial stage, a linear chain propagation was observed with a low polydispersity (< 1.35) demonstrating the controlled/living polymerization feature. However, the products obtained during this stage showed a high consumption of pendent vinyl groups (around 28%) based on the analysis by proton nuclear magnetic resonance (H-1-NMR). This high pendent vinyl conversion in the linear chain propagation stage is attributed to the significant involvement of the intramolecular cyclization. The promotion of the intramolecular cyclization and suppression of the intermolecular crosslinking is achieved by the low kinetic chain length and low polymer volume concentration. Given the coexistence of linear chain propagation and high pendent vinyl conversion, the novel single chain cyclized polymer structure was formed during this process, which was further used as polymeric nanoparticles to modify the viscoelasticity of linear poly(methyl methacrylate) (PMMA) melts. The essentially similar chemical structure between the EGDMA and MMA ensures the minimization of enthalpic interactions and dispersion forces between the nanoparticles and linear melts. The oscillatory rheology study and the subsequent time temperature superposition based on the Williams-Landel-Ferry equation demonstrated the coexistence of the segmental relaxation at high frequencies and chain relaxation at low frequencies. The complex viscosity studied as a function of the shear frequency showed the decrease in terminal viscosity with addition of 10 wt% single chain cyclized polyEGDMA nanoparticles. A further decrease was also observed with the addition of 20 wt% nanoparticles, which is not in agreement with Einstein relationship between the complex viscosity and fraction of added particles. This strategy provides a simple and efficient approach to control polymerization of multivinyl monomers, and the unexpected decrease in viscosity of the blend system should in principle open a new avenue to modify polymer melts and molten systems.