Effect of pre-sintering particle size on the microstructure and magnetic properties of two-step hot-press prepared BaFe 12 O 19 thick films

Anjiang Dong,Ranyang Liu,Zeqiang Tian,Feng Peng,Run Zhao,Xiaodong Su,Rujun Tang

DOI: https://doi.org/10.1016/j.jallcom.2023.171683

IF: 6.2

2023-08-12

Journal of Alloys and Compounds

Abstract:Both particle size and processing conditions can affect the magnetic properties of ferrite materials. In this work, the two-step hot-press procedures (hot-press magnetic orientation followed by hot-press sintering) is designed for fabrication of high quality BaFe 12 O 19 thick films. The effects of pre-sintering particle size (G pre ) on the microstructure and magnetic properties of the thick films are investigated. Results show that reducing G pre increase c -axis orientation and remanence ratio (RR) of sintered thick film greatly. This should be due to the reduced energy barriers for grain orientation during the hot-press magnetic orientation process. Decreasing G pre from 920 nm to 170 nm leads to larger coercivity (H c ), while the saturation magnetization does not change notably above G pre = 170 nm. The H c mechanism is further analyzed by the G pre dependent anisotropy field H k and the first-order-reversal curves of the thick film. Results show that H k increases with reducing G pre , while the inter-grain interactions are not notably affected by G pre . Therefore, the increase of H c should be contributed by both the decrease of sintered particle size and the improved RR of the film after hot-press magnetic field orientation. The above results show that the two-step hot-press sintering prepared hexaferrite thick films with optimized G pre is a good candidate for the realization of self-biased high frequency devices.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering