Abstract:The grain boundary diffusion process (GBDP) is effective to enhance coercivity of the single-main-phase (SMP) RE2Fe14B (rare earth (RE)) magnets through forming magnetic hardening shells surrounding the hard grain cores. Here, the GBDP was applied to the multi-main-phase (MMP) (Nd, Pr)(22.3)Ce8.24Feba1M1.0B1.0 (wt.%) magnets prepared by sintering the mixture of Ce-free and Ce-containing 2:14:1 powders, which have shown superior magnetic properties, especially coercivity, to the SMP ones at the same average composition. The remanence of the (Nd, Pr)H-x diffused magnets increases gradually with the increase of diffusion temperature from 480 to 880 degrees C, the coercivity, however, slightly decreases. The highest (BH)(max) of 350.1 kJ m(-3) is achieved when diffusing at 680 degrees C, which is 9.2% higher than 320.7 kJ m(-3) for the as-prepared magnet. The remanence increment is due to the diffusion of Nd/Pr into the 2:14:1 phase grains, enlarging the intrinsic saturation magnetic polarization. The slight coercivity reduction is due to the gradual homogenization of RE distribution within the 2:14:1 grains of the undiffused parts, i.e. approaching the 'close to equilibrium (or SMP)'state, which offsets the positive contributions from the enrichment of Nd/Pr in the Ce-rich 2:14:1 phase and the formation of continuous RE-rich intergranular phase. These findings suggest that the GBDP effect on coercivity of the MMP Nd-Ce-Fe-B magnets is distinctly different from the SMP ones, and that the chemical heterogeneity should be carefully controlled to improve the magnetic properties of such high cost-performance permanent magnets.

Realization of high-performance HRE-free Pr-Fe-B sintered magnet through microstructure regulation

Comparison of (pr, Nd)H Grain Boundary Restructuring and Diffusion on the Magnetic Properties of Nd–La–Ce–Fe–B Sintered Magnet

Design and fabrication of Dy-free sintered permanent magnets with high coercivity

High-Remanence Fe-Rich 2:17-Type Sm-Co Sintered Magnets Mediated Via Multiscale Microstructure

Research on the La/Ce-rich multi-main-phase RE-Fe-B permanent magnetic materials

Magnetic performance change of multi-main-phase Nd–Ce–Fe–B magnets by diffusing (Nd, Pr)H x

Nd-Fe-B Sintered Magnets with Low Rare Earth Content Fabricated Via Dy71.5Fe28.5 Grain Boundary Restructuring

Construction of High-Performance Multi-Main-phase Nd–Dy–Fe–B Sintered Magnets with Strengthened Chemical Heterogeneity

Achievement of high performance in multi-main-phase (Pr,Nd,MM)-Fe-B sintered magnets by regulating microstructure

Coercivity Enhancement of Low Rare Earth Nd–Fe–B Sintered Magnets by Optimizing Microstructure

A practical method to enhance the properties of Pr/Nd-lean sintered RE-Fe-B magnets: high entropy design for RE 2 Fe 14 B

High remanence Fe‐rich 2:17‐type Sm‐Co sintered magnets mediated via multi‐scale microstructure

High-coercivity heavy-rare-earth-free NdFeB sintered magnets developed by doping Ce85Al15 and grain boundary diffusion with Pr70Cu15Al15

Grain boundary restructuring of the (Misch Metal, Nd)-Fe-B sintered magnet using Pr82Co18 powders

Enhancement of Magnetic Properties and Corrosion Resistance for Misch Metal Based RE-Fe-B Magnets Prepared by Double Main Phase Process

Optimization of the core-shell structures and grain boundary to improve the coercivity of high Ce-content Nd-Ce-Fe-B magnets

A practical method to enhance the properties of Pr/Nd-lean sintered RE-Fe-B magnets: High entropy design for RE2Fe14B

Enhanced Coercivity of Nd-Ce-Fe-B Sintered Magnets by Adding (nd, Pr)-H Powders

Preparation of Highly Textured Hydrogenation-Disproportionation-desorption-recombination Powders for Nd-Fe-B Sintered Magnets

Grain boundary engineering towards high-figure-of-merit Nd-Ce-Fe-B sintered magnets: Synergetic effects of (Nd, Pr)Hx and Cu co-dopants

Development of Dy-Free Nd–Fe–B-Based Sintered Magnet Through Grain Boundary Engineering Using Pr–Cu Alloys