Abstract:The effects of incorporating dilute Gd and Ce on the microstructure and mechanical properties of Mg-0.5Sn-0.3Zn (TZ00, wt%) alloys are systematically revealed. The results indicate that the co-addition of 0.3 wt% Gd and 0.3 wt% Ce can significantly reduce the grain size from 40.8 μm to 12.0 μm, enhance dynamic recrystallization, and attenuate the intensity of basal texture. Furthermore, plenty of micron- and nano-scale (Gd, Ce)MgSn phases are precipitated. In comparison with the TZ00 alloy, the Mg-0.5Sn-0.3Zn-0.3Gd-0.3Ce alloy (TZGE0000, wt%) displays synergistic improvements in strength and ductility. The corresponding tensile yield strength (TYS), ultimate tensile strength (UTS), and elongation (EL) are 214.1 MPa, 297.4 MPa, and 23.5 %, respectively. The primary reason for this strength improvement is the combined effects of grain refinement and (Gd, Ce)MgSn nano-phase strengthening, while the ductility enhancement is mainly due to the refined grain size, weakened basal texture, increased activation of prismatic slip and {10−12} tensile twinning. Additionally, relative Visco-Plastic Self-Consistent (VPSC) simulations confirm that the combined addition of Gd and Ce can promote the activation of non-basal slip and {10−12} tensile twinning during the deformation process. In more detail, basal and prismatic slips are the primary deformation mechanisms during tensile loading, together with a minor occurrence of {10−12} tensile twinning and pyramidal slip coordination deformations. Conversely, {10−12} tensile twinning predominates during the compression deformation.

Enhanced Strength-Ductility Synergy in Mg-0.5 wt%Ce Alloy by hot Extrusion

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Achieving high strength-ductility synergy in dilute Mg-Al-Ca alloy by trace Ce addition

Mechanical properties of Mg-Ce-Y-Zr-Zn-Ca microalloyed magnesium alloys composed of near-atomic solute

Effect of cerium alloying on microstructure, texture and mechanical properties of magnesium during cold-rolling process

Effect of Ce Addition on the Microstructure, Thermal Conductivity and Mechanical Properties of Mg–0.5Mn Alloys

Effect of Ce Addition on Modifying the Microstructure and Achieving a High Elongation with a Relatively High Strength of As-Extruded AZ80 Magnesium Alloy

Influence of Ce content on the microstructures and tensile properties of Mg-1Gd-0.5Zn alloys

Effect of Sm and Ce content on microstructure and mechanical property of newly developed Mg-Sm-Ce-Mn based alloy

Synergistic effect of Gd and Ce on enhancement of mechanical properties of as-extruded Mg-Sn-Zn alloys

Development of novel lightweight and cost-effective Mg–Ce–Al wrought alloy with high strength

Effect of Ce Addition on Microstructure, Thermal Conductivity, and Mechanical Properties of As-Cast and As-Extruded Mg–3Sn Alloys

Towards reducing tension-compression yield and cyclic asymmetry in pure magnesium and magnesium-aluminum alloy with cerium addition

Influence of Processing Routes to Enhance the Mechanical Properties of Mg–6Zn–1Y–3.5CeMM (wt.%) Alloy

Effect of pre-stretching on enhancing yield strength of as-extruded Mg-Sm-Ce based alloy

Influence of Ca-Ce/La synergistic alloying on the microstructure and mechanical properties of extruded Mg–Zn alloy

Enhanced strength-ductility synergy and activation of non-basal slip in as-extruded Mg–Zn–Ca alloy via heterostructure

Tailoring strength and ductility of Mg97Y2Zn1 alloy through the architecture of heterogeneous lamellar structure by large-ratio hot extrusion

Effect of Extrusion Temperature on the Microstructure and Thermal Conductivity of Mg–2.0Zn–1.0Mn–0.2Ce Alloys

Preparation of ultrafine-grained Mg–Mn–Ce alloy with high ductility and energy absorption by coupling extrusion and forging

Achieving High Strength-Ductility Synergy in Low-Alloyed Mg-Li-Er Extrusion Alloys via Tailoring Bimodal-Grained Structure