Evaluating the Influence of Copper Bar Preheating Temperature on the Electromechanical and Microstructural Characteristics of In Situ Heat-Treated 7075Al/Cu Composite Joints

Muhammad Waqas Hanif,Muhammad Sajid,Muhammad Jawad,Wasim Ahmad

DOI: https://doi.org/10.1007/s11665-024-10417-6

IF: 2.3

2024-11-21

Journal of Materials Engineering and Performance

Abstract:This research focuses on optimizing the mechanical and electrical properties of 7075 Al/Cu composite joints produced through the squeeze casting process. The effect of three key input parameters, such as copper bar preheating temperature ( T C ), melt temperature ( T M ), and squeeze pressure ( S P ) on electrical resistance (ER), micro-hardness (MH), and ultimate tensile strength (UTS) has been analyzed. The response surface methodology (RSM) and artificial neural network (ANN) methods have been used to structure the input parameters, which allows the modeling of the input parameters to predict the optimal output response. Analysis of variance results indicated that T M significantly influenced the ER, whereas UTS and MH are predominantly affected by S P . Optimal values of the UTS of 60.10 MPa, MH of 86.11 HV, and ER of 2.240 μΩ have been achieved at T C of 300 °C, T M of 780 °C, and S P of 90 MPa. The scanning electron microscope analysis proved that the diffusion rate of Cu atom into the Al melt has increased significantly at the optimal experimental settings, which has prominently improved the electro-mechanical properties of the Al/Cu composite joints. The fractography analysis revealed a brittle fracture surface with a substantially flat facet morphology at optimal conditions. In contrast, energy-dispersive spectroscopy revealed a zinc content of 0.83% by weight at the interface region of Al/Cu that witnessed an appropriate zinc melting. X-ray diffraction highlighted the role of T C and T M in forming strong and high-conductive Al–Cu eutectic phases, which enhanced the strength and electrical conductivity of Al/Cu composite joints. Moreover, comparative analysis of ANN and RSM demonstrated an improvement in the R -square values by 1%, 2.01%, and 10.24% and a reduction in the mean squared error (MSE) by 42.58%, 39.35%, and 37.29% for ER, MH, and UTS, respectively, have been found through ANN modeling approach.

materials science, multidisciplinary