Effect of an external magnetic field on the interaction of carbon monoxide with hematite.

Petr Chernavskii,Galina Viktorovna Pankina

DOI: https://doi.org/10.1039/d4cp01249f

IF: 3.3

2024-05-28

Physical Chemistry Chemical Physics

Abstract:The effect of an external magnetic field on the activation energy (E*) of carbon monoxide interaction with hematite under isothermal conditions in the temperature range of 250 to 350°C has been studied by in situ magnetometry. The dependence of E* of the reaction of magnetite formation on the magnetic field strength in the field strength range from 60 Oe to 3 kOe is shown for samples of hematite nanoparticles deposited on silica gel with sizes of 20 nm. The extreme field dependence of E* was found. 1.IntroductionThe CO + hematite reaction is the key reaction in the formation of active centers ofiron-loaded catalysts for Fischer-Tropsch synthesis [1-4]. Essentially, the first stepinvolves the oxidation of CO adsorbed on the hematite surface to CO2, resulting inthe reduction of hematite to magnetite. The subsequent reaction of CO withmagnetite results in the formation of carbides of varying composition [5-11]. Theprocess of CO oxidation on dispersed hematite particles is also used to remove lowconcentrations of CO from gas mixtures [12-13]. In this case, hematite plays the roleof a catalyst when a CO-O2 gas mixture is used. The study of the process kinetics[13] showed that the activation energy was estimated to be 19.0 ± 0.14 kJ/mole. Thereaction rate increases with increasing temperature and CO content in the feed gas.The kinetics of hematite reduction by CO has also been studied in [14-16]. Theactivation energy of the Fe2O3 + CO → Fe3O4 + CO2 reaction varies from 33.28 to 74.00 kJ/mol [17]. It should be noted that in the overwhelming number of works devoted to the kinetics of hematite reduction by carbon monoxide, the reaction is considered on the example of massive Fe2O3 particles.

chemistry, physical,physics, atomic, molecular & chemical