Reduction Kinectics of Hematite Powders in Non-Equilibrium Hydrogen Plasma

Iraldo Sá Silveira,Estéfano Aparecido Vieira,Ramiro Conceição Nascimento,Adonias Ribeiro Franco Júnior,Jaime Alberto Sanchez Caceres
DOI: https://doi.org/10.1590/1980-5373-mr-2023-0496
2024-06-25
Materials Research
Abstract:Silveira, Iraldo Sá ; Vieira, Estéfano Aparecido ; Nascimento, Ramiro Conceição ; Franco Júnior, Adonias Ribeiro ; Caceres, Jaime Alberto Sanchez ; The reduction kinetics of hematite (Fe2O3) powders was studied using nonequilibrium hydrogen plasma as reducing agent. Reduction experiments were performed in a DC pulsed plasma reactor, hydrogen flow-rate of 300 cm3/min, at pressure of 400 Pa, reduction times in range 30-120 minutes and in temperatures range 320-380 °C. Fe2O3 powders after reduction experiments were characterized by X-ray diffraction, weight loss of oxygen (gravimetric analyses), optic microscope and scanning electron microscope. The results showing that the reduction temperature of 380 °C after 120 min allows obtaining α-iron with a reduction fraction of about 0.93. The powder particles are transformed into two steps: Fe2O3→Fe3O4→Fe-α. The activation energy experimentally established for the reduction of Fe2O3 was about 98.4 kJ/mol.
materials science, multidisciplinary
What problem does this paper attempt to address?