Abstract:Iron ore pellet reduction experiments were performed with pure hydrogen (H2) and mixtures with carbon monoxide (CO) at different ratios. For direct reduction processes that switch dynamically between reformed natural gas and hydrogen as the reductant, it is important to understand the effects of the transition on the oxide reduction kinetics to optimize the residence time of iron ore pellets in a shaft reactor. Hence, the reduction rates were studied by varying experimental parameters such as the temperature (800, 850 & 900 °C), reactant gas flow rate (100, 150 & 200 cm3/min), pellet size and composition of the reactant gas mixture. The rate of reduction was observed to increase with an increase in temperature and reactant gas flow rate, but it decreased with an increase in pellet size. SEM greyscale analysis was performed to analyze the porosity and phase composition of partially reduced pellets. The porosity of the pellets was observed to increase from 0.3 for unreacted pellet to 0.42 for a completely reduced pellet. Energy-dispersive X-ray spectroscopy (EDAX) analysis was performed to identify the phases observed in the SEM images. The fraction of iron phase was observed to increase from the shell region of the pellet to the core region with an increase in the degree of reduction. A 2D-axisymmetric numerical model was developed on COMSOL Multiphysics, and it was validated using the conversion (X) vs. time curves obtained from each experiment. The model was able to accurately predict the total time needed for the complete conversion of a single iron ore pellet for multiple experiments. Effects of changes in the porosity and tortuosity of the pellet on the model were also studied and the rate of reduction was observed to be sensitive to changes in both porosity and tortuosity. The SEM analysis and the model results show that tortuosity is higher for pellets reduced with H2 than for pellets reduced with H2-CO gas mixtures.

Studies on the Reduction Behavior of Iron Oxide Pellet Fines with Hydrogen Gas: Mechanism and Kinetic Analysis

A Laboratory Study of the Reduction of Iron Oxides by Hydrogen

Kinetic Analysis of Isothermal and Non-Isothermal Reduction of Iron Ore Fines in Hydrogen Atmosphere

Kinetic analysis of iron ore powder reaction with hydrogen—carbon monoxide

Kinetics and microstructural changes during fluidized reduction of magnetite with hydrogen at low temperatures

On the Kinetic Mechanisms of the Reduction and Oxidation Reactions of Iron Oxide/Iron Pellets for a Hydrogen Storage Process

Kinetic Mechanism Development for the Direct Reduction of Single Hematite Pellets in H2/CO Atmospheres

Investigation of reduction behavior of various iron ores in a hydrogen-rich reducing atmosphere

Hydrogen-based direct reduction of combusted iron powder: deep pre-oxidation, reduction kinetics and microstructural analysis

Investigation of (H2–H2O) partial pressure on the gas-based reduction of fine iron ore in mixed gases (H2–H2O–CO–CO2–N2)

Study on the reduction of Fe2O3 pellets by CO-CO2 and H2-H2O: Reaction kinetics and pore network model

Effect of Hydrogen-Rich Atmosphere on the Reduction Behavior and Kinetics of Iron-Ore Pellets Under Non-isothermal Conditions

Modeling Isothermal Reduction of Iron Ore Pellet Using Finite Element Analysis Method: Experiments & Validation

Reduction kinetics of iron oxide pellets with H2 and CO mixtures

A Review on the Kinetics of Iron Ore Reduction by Hydrogen

Kinetic Analysis of the Iron Oxide Reduction Using Hydrogen-Carbon Monoxide Mixtures as Reducing Agent

Reduction Kinetics of Oxidized New Zealand Ironsand Pellets in H2 at Temperatures up to 1443 K

Optimization of Hydrogen Utilization and Process Efficiency in the Direct Reduction of Iron Oxide Pellets: A Comprehensive Analysis of Processing Parameters and Pellet Composition

Results of Hydrogen Reduction of Iron Ore Pellets at Different Temperatures

The Direct Reduction of Iron Ore with Hydrogen

Green Ironmaking at Higher H2 Pressure: Reduction Kinetics and Microstructure Formation During Hydrogen-Based Direct Reduction of Hematite Pellets