Optimization of Hydrogen Utilization and Process Efficiency in the Direct Reduction of Iron Oxide Pellets: A Comprehensive Analysis of Processing Parameters and Pellet Composition

Angelo Perrone,Pasquale Cavaliere,Behzad Sadeghi,Leandro Dijon,Aleksandra Laska

DOI: https://doi.org/10.1002/srin.202400565

IF: 2.1258

2024-10-17

steel research international

Abstract:This study investigates the optimization of hydrogen consumption in the direct reduction of iron oxide pellets, focusing on the effects of process parameters such as temperature, gas flow, and pellet composition. The results show how certain pellet compositions and operating conditions can minimize hydrogen consumption and improve the efficiency and sustainability of steel production. The article deals with the H2 consumption for different processing conditions and the composition of the processed pellets during the direct reduction process. The experiments are carried out at 600–1300 °C, with gas pressures of 1–5 bar, gas flow rates of 1–5 L min−1, and basicity indices of 0 to 2.15. Pellets with different compositions of TiO2, Al2O3, CaO, and SiO2 are analyzed. The gas flow rate is crucial, with 0–10 L min−1 leading to an H2 consumption of 0–5.1 kg H2/kg pellet. The gas pressure (0–10 bar) increases the H2 consumption from 0 to 5.1 kg H2/kg pellet. Higher temperatures (600–1300 °C) reduce H2 consumption from 5.1 to 0 kg H2/kg pellet, most efficiently at 950–1050 °C, where it decreases from 0.22 to 0.10 kg H2/kg pellet. An increase in TiO2 content from 0% to 0.92% lowers H2 consumption from 0.22 to 0.10 kg H2/kg pellet, while a higher Fe content (61–67.5%) also reduces it. An increase in SiO2 content from 0% to 3% increases H2 consumption from 0 to 5.1 kg H2/kg pellet. Porosity structure influences H2 consumption, with the average pore size decreasing from 2.83 to 0.436 mm with increasing TiO2 content, suggesting that micropores increase H2 consumption and macropores decrease it.

metallurgy & metallurgical engineering