High Toughness and CMAS Resistance of REAlO3/RE2Zr2O7 (RE = La, Nd, Sm, Eu, Gd, and Dy) Composites with Eutectic Composition for Thermal Barrier Coatings
Zijian Zhang,Jian Sun,Guanghua Liu,Yi Han,Wei Liu,Yi Li,Wei Wang,Xiangyang Liu,Peng Zhang,Wei Pan,Chunlei Wan
DOI: https://doi.org/10.26599/jac.2024.9220899
IF: 11.534
2024-01-01
Journal of Advanced Ceramics
Abstract:Although rare earth zirconates (RE2Zr2O7) have garnered attention as viable candidates for thermal barrier coatings (TBCs), they suffer from low fracture toughness and accelerated calcium-magnesium-alumina-silicate (CMAS) melt corrosion at high service temperatures, which impedes their practical application. In this work, we developed a series of REAlO3/RE2Zr2O7 (RE = La, Nd, Sm, Eu, Gd, and Dy) composites with a eutectic composition that not only significantly enhanced the fracture toughness by more than 40% relative to that of RE2Zr2O7 but also exhibited improved resistance to CMAS corrosion. The increase in toughness arises from multiple mechanisms, such as ferroelastic toughening, fine-grain strengthening, and residual stress toughening, all of which trigger more crack defects and energy consumption. Additionally, the CMAS penetration depth of the REAlO3/RE2Zr2O7 composites is approximately 36% lower than that of RE2Zr2O7. Al-O constituents in composites can capture CaO, SiO2, and MgO in CMAS melts and increase their viscosity, resulting in enhanced CMAS corrosion resistance. The thermophysical properties of the REAlO3/RE2Zr2O7 composites were also investigated, and their coefficient of thermal expansion and thermal conductivity are comparable to those of 7-8 wt %Y2O3 partially stabilized ZrO2 (YSZ), indicating their potential as TBC materials.