Abstract:Abstract Y 2 O 3 is regarded as one of the potential environmental barrier coating (EBC) materials for Al 2 O 3f /Al 2 O 3 ceramic matrix composites owing to its high melting point and close thermal expansion coefficient to Al 2 O 3 . However, the relatively high thermal conductivity and unsatisfactory calcium-magnesium-aluminosilicate (CMAS) resistance are the main obstacles for the practical application of Y 2 O 3 . In order to reduce the thermal conductivity and increase the CMAS resistance, four cubic bixbyite structured high-entropy oxides RE 2 O 3 , including (Eu 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 , (Sm 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 , (Sm 0.2 Eu 0.2 Er 0.2 Y 0.2 Yb 0.2 ) 2 O 3 , and (Sm 0.2 Eu 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 were designed and synthesized, among which (Eu 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 and (Sm 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 bulks were prepared by spark plasma sintering (SPS) to investigate their mechanical and thermal properties as well as CMAS resistance. The mechanical properties of (Eu 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 and (Sm 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 are close to those of Y 2 O 3 but become more brittle than Y 2 O 3 . The thermal conductivities of (Eu 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 and (Sm 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 (5.1 and 4.6 W·m −1 ·K −1 ) are only 23.8% and 21.5% respectively of that of Y 2 O 3 (21.4 W·m −1 ·K −1 ), while their thermal expansion coefficients are close to those of Y 2 O 3 and Al 2 O 3 . Most importantly, HE RE 2 O 3 ceramics exhibit good CMAS resistance. After being attacked by CMAS at 1350 °C for 4 h, the HE RE 2 O 3 ceramics maintain their original morphologies without forming pores or cracks, making them promising as EBC materials for Al 2 O 3f /Al 2 O 3 composites.

High Toughness and CMAS Resistance of REAlO3/RE2Zr2O7 (RE = La, Nd, Sm, Eu, Gd, and Dy) Composites with Eutectic Composition for Thermal Barrier Coatings

Preparation and properties of CMAS resistant bixbyite structured high-entropy oxides RE2O3 (RE = Sm, Eu, Er, Lu, Y, and Yb): Promising environmental barrier coating materials for Al2O3f/Al2O3 composites

Improved thermal properties and CMAS corrosion resistance of high-entropy RE zirconates by tuning fluorite-pyrochlore structure

Rare-earth high-entropy aluminate-toughened-zirconate dual-phase composite ceramics for advanced thermal barrier coatings

High-entropy rare-earth zirconate ceramics with low thermal conductivity for advanced thermal-barrier coatings

A novel dual-phase high-entropy (La0.2Nd0.2Gd0.2Er0.2Yb0.2)2Zr2O7 ceramic for thermal barrier coatings applications: Preparation, microstructure, and thermo–physical properties

Towards Thermal Barrier Coating Application for Rare Earth Silicates RE2SiO5 (RE = La, Nd, Sm, Eu, and Gd)

CMAS corrosion behavior of a novel high entropy (Nd0.2Gd0.2Y0.2Er0.2Yb0.2)2Zr2O7 thermal barrier coating materials

Effect of Yb2O3 Doping on the Thermal and Mechanical Properties GdAlO3-Gd2Zr2O7 Composite with Eutectic Composition

An investigation into RESZ (RE = Yb, Er, Gd, Sm) materials for CMAS resistance in thermal barrier coatings

CMAS corrosion resistant of La3+-Yb3+-Ce4+ co-doped ZrO2 based TBCs: Experimental and theoretical research

Calcium-magnesium-alumina-silicate (CMAS) resistant high entropy ceramic (Y0.2Gd0.2Er0.2Yb0.2Lu0.2)2Zr2O7 for thermal barrier coatings

Pronounced Enhancement of Thermal Expansion Coefficients of Rare-Earth Zirconate by Cerium Doping

Reaction mechanisms of (RE0.2Nd0.2Sm0.2Eu0.2Gd0.2)2Zr2O7 (RE = La or Yb) under CaO-MgO-Al2O3-SiO2 (CMAS) attack

Mechanical Properties and CMAS Corrosion Resistance of La2Ce2O7/YSZ Composite Thermal Barrier Coatings

Equimolar YO 1.5 and TaO 2.5 co‐doped ZrO 2 as a potential CMAS‐resistant material for thermal barrier coatings

High Temperature Corrosion of (er0.25tm0.25yb0.25lu0.25)2si2o7 Environmental Barrier Coating Material Subjected to Water Vapor and Molten Calcium–magnesium–aluminosilicate (CMAS)

Rare-earth cerates with a high coefficient of thermal expansion and excellent CMAS corrosion resistance obtained through high-entropy designing

Research on Modified Thermal Barrier Coatings Against CMAS Corrosion Driven by Mechanism–Data Hybrid Model

Interaction laws of RE 2 O 3 and CMAS and rare earth selection criterions for RE-containing thermal barrier coatings against CMAS attack

Multicomponent rare-earth cerate and zirconocerate ceramics for thermal barrier coating materials