Abstract:We have studied the catalytic carbon monoxide (CO) oxidation (CO+0.5O2→CO2) reaction using a powder catalyst composed of both copper (5wt.% loading) and titania (CuOx–TiO2). Our study was focused on revealing the role of Cu, and the interaction between Cu and TiO2, by systematic comparison between two nanocatalysts, CuOx–TiO2 and pure CuOx. We interrogated these catalysts under in situ conditions using X-ray diffraction (XRD), X-ray absorption fine structure (XAFS) and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) to probe the structure and electronic properties of the catalyst at all stages of the reaction and simultaneously probe the surface states or intermediates of this reaction. With the aid of several ex situ characterization techniques including transmission electron microscopy (TEM), the local catalyst morphology and structure were also studied. Our results show that a CuOx–TiO2 system is more active than bulk CuOx for the CO oxidation reaction due to its lower onset temperature and better stability at higher temperatures. Our results also suggest that surface Cu+ species observed in the CuOx–TiO2 interface are likely to be a key player in the CO oxidation mechanism, while implicating that the stabilization of this species is probably associated with the oxide–oxide interface. Both in situ DRIFTS and XAFS measurements reveal that there is likely to be a Cu(Ti)–O mixed oxide at this interface. We discuss the nature of this Cu(Ti)–O interface and interpret its role on the CO oxidation reaction.

A local hydroxyl group-modified copper site directs the oxidation of carbon monoxide

Large-scale Synthesis and Catalytic Activity of Nanoporous Cu–O System Towards CO Oxidation

Site‐Resolved Cu2O Catalysis in the Oxidation of CO

CO oxidation over CuOx/TiO2 catalyst: The importance of oxygen vacancies and Cu+ species

Oxidation of carbon monoxide catalyzed by copper-zirconium composite oxides

Elucidating the Nature of the Cu(I) Active Site in CuO/TiO2 for Excellent Low-Temperature CO Oxidation

Interfacial Cu+ promoted surface reactivity: Carbon monoxide oxidation reaction over polycrystalline copper–titania catalysts

CuO/TiO 2 /Ti Monolithic Catalysts for Low-Temperature CO Oxidation

Surface Structure Characteristics of CuO/Ti0.5Sn0.5O2 and Its Activity for CO Oxidation

Nature of Copper Active Sites in the Carbon Monoxide Oxidation on CuAl2O4and CuCr2O4Spinel Type Catalysts

On the Role of Hydroxyl Groups on Cu/Al 2 O 3 in CO 2 Hydrogenation

Hetero-metal Cation Control of CuO Nanostructures and Their High Catalytic Performance for CO Oxidation.

Catalytic oxidation of CO over CuO@TiO2 catalyst: The relationship between activity and adsorption performance

Promotional Effects of Cu O on the Activity of Cu/ZnO Catalyst Toward Efficient CO Oxidation

Facile synthesis of a CuMnO<sub><i>x</i></sub> catalyst based on a mechanochemical redox process for efficient and stable CO oxidation

Enhancing CO catalytic oxidation performance over Cu-doping manganese oxide octahedral molecular sieves catalyst

Effect of the preparation method on the performance of CuO-MnO x-CeO 2 catalysts for selective oxidation of CO in H 2-rich streams

Nature of Reactive Oxygen Intermediates on Copper-Promoted Iron–Chromium Oxide Catalysts During CO2 Activation

Unraveling distinct effects between CuOx and PtCu alloy sites in Pt-Cu bimetallic catalysts for CO oxidation at different temperatures

Copper Manganese Oxides Supported on Multi-Walled Carbon Nanotubes As an Efficient Catalyst for Low Temperature CO Oxidation

CO Oxidation over Alumina-Supported Copper Catalysts