Abstract:Pure copper is very soft, however, hardening the pure copper with most strengthening mechanisms leads to a significant reduction in electrical conductivity. Grain refinement is a better strengthening mechanism to maintain high enough electrical conductivity. Plastic deformation at room temperature followed by post-annealing is one of the best methods to achieve fine-grained metals and alloys. In this research, the high-temperature annealing behavior of cold-rolled electrolytic tough-pitch (ETP) copper sheets was studied. 90 % asymmetric cold rolling followed by high-temperature post-annealing at 673 K for 1, 2, 5, 10, 30, 60, and 120 min were applied on the copper. The microstructure was significantly changed with increasing annealing time from 1 to 2 min owing to full recrystallization. With increasing the annealing duration, the grain size is increased. The formation of equiaxed grains with a smaller size (∼9 μm) compared to the full-annealed (initial) sample (∼68 μm) is observed after the longest time of post-annealing (120 min) due to the pinning effect of Cu2O particles. The post-annealed copper sheets processed by asymmetric rolling (in this work) exhibited a more homogeneous microstructure through the thickness compared to the symmetric rolling due to more uniform stored strain energy. The results showed that the first deformed grains that undergo recrystallization during post-annealing are Goss-oriented grains. With an increase in the post-annealing time, the S and Copper components were eliminated and a strong Cube and P texture orientations were formed. Interestingly, after 1 min of post-annealing, the yield and tensile strength enhanced to 410.2 MPa and 418.6 MPa owing to the annealing hardening phenomenon. The hardness and strength reached a constant value after the post-annealing for 10 min and above. With increasing the post-annealing duration, the central area of fracture surfaces (consisting of ductile dimples) became larger and the outer region (consisting of flat surfaces and shear dimples) became smaller, showing a shift towards perfect ductile fracture. With the increase of post-annealing time from 1 min to 120 min, the electrical conductivity was increased from 77.6 to 97.5 %IACS. The presence of the Cube texture increased the electron mobility compared to the P orientation, by reducing the mean distance that they can travel without scatter. From the obtained results, it can be concluded that the asymmetric cold rolling followed by high-temperature post-annealing is capable of strength improvement and maintaining electrical conductivity in copper.

Investigating the combined influence of rolling, ECAP processes, and intermediate annealing on mechanical and microstructural properties of beryllium copper alloy 25

Investigating the Influence of Thermomechanical Equal Channel Angular Pressing (ECAP) Improved Die on AA-6061

Design and analysis of ECAP Processing for Al6061 Alloy: a microstructure and mechanical property study

Experimental and Numerical Investigation of the ECAP Processed Copper: Microstructural Evolution, Crystallographic Texture and Hardness Homogeneity

Characterization of microstructural evolution and mechanical properties of Cu-Ni-Cr alloys deformed by ECAP

Influence of Equal Channel Angular Pressing Technique on Mechanical Properties, Corrosion Resistance, and Microstructural Behavior of Al-Alloy 5083

Mechanical and microstructural characteristics of AA6082 using thermal equal channel angular pressing for structural applications

Intermediate Annealing of Pure Copper During Cyclic Equal Channel Angular Pressing

Microstructure, texture and mechanical properties of pure copper processed by ECAP and subsequent cold rolling

Microstructure Evolution and Mechanical Properties of a Ti–35Nb–3Zr–2Ta Biomedical Alloy Processed by Equal Channel Angular Pressing (ECAP)

Development of mechanical properties and microstructure for Al–Zn–Mg–Cu alloys through ECAP after optimizing the outer corner angles through FE modeling

Effects Of Ecap And Annealing Treatment On The Microstructure And Mechanical Properties Of Mg-1y (Wt. %) Binary Alloy

Microstructure Evolution and Cooperative Strengthening Mechanism of Copper–Aluminum Bimetal Continuous Equal Channel Angular Pressing-Annealing Process

Tribological and mechanical behavior of AL 2014 aluminum alloy influenced by microstructure and texture evolution after equal channel angular processing

Effects of Annealing Treatment on Mechanical and Tribological Performance of Cu–10Al–4Fe after Equal Channel Angular Extrusion

Influence of Equal Channel Angular Pressing and Cyclic Extrusion Compression on the Microstructure Evolution and Mechanical Properties of Pure Aluminum

High-temperature annealing behavior of cold-rolled electrolytic tough-pitch copper

Conjoint influence of equal channel angular pressing and annealing on microstructure and mechanical properties of aluminum alloy 7075Gemeinsamer Einfluss des Gleichkanal‐Winkelpressens und des Glühens auf das Gefüge und die mechanischen Eigenschaften der Aluminiumlegierung EN AW‐AlZn5,5MgCu

Analysis of mechanical and microstructural characteristics of plunger-assisted ECAP strengthened Ti-6Al-4V alloy sheets

Microstructural evolution and mechanical properties of AZ31 Mg alloy fabricated by a novel bifurcation-equal channel angular pressing

Microstructure and Mechanical Evolution of Cu-2.7Be Sheets Via Annealing