Design and analysis of ECAP Processing for Al6061 Alloy: a microstructure and mechanical property study

Ankita Awasthi,Kuldeep K Saxena,R. K. Dwivedi,Dharam Buddhi,Kahtan A. Mohammed

DOI: https://doi.org/10.1007/s12008-022-00990-2

2022-08-04

International Journal on Interactive Design and Manufacturing (IJIDeM)

Abstract:In this study, equal channel angular pressing (ECAP) method is used to obtain fine grain microstructure in Al 6061 alloy at room and elevate temperatures. The billet samples are allowed to pass through die channel. Die design parameters such as die angle, corner angle, passing route, number of passes, plunger speed are taken into account in order to obtain the recorded grain refinement. It is seen that grain structure changes, the mechanical properties such as hardness, tensile strength of material also changes. A metallurgical optical microscope is used to capture the microstructure pattern. The ECAP technique performed at different processing conditions such as one pass, three pass and six pass at room temperature and elevated temperature. The route BC is used to pass the sample through the die because BC route provide elongated and equiaxed grains. The experimentally recorded tensile strength of one pass, three pass and six pass ECAP processed are 233 MPa, 184 MPa and 215 MPa respectively. The results reveal that there is a remarkable percentage change observed in tensile strength of processed samples before and after ECAP process are 121.9%, 75.2% and 104.7% respectively. Likewise, micro hardness value found to be increase as a function of passes on ECAP process.