Abstract:Direct ink writing of thermosetting materials, e.g. epoxy resin, is a promising technique for the rapid and low-cost fabrication of high-strength parts with complex geometry. In this study, a microwave-assisted 3D printer using rectangular waveguide (RWG) was developed to overcome the ink's low viscosity and slow curing speed. Microwave curing and ink extrusion are synchronous to improve shape retention of ink. The critical structure parameters of the RWG applicator were determined using the multiphysics simulation to achieve optimal microwave system matching and ink heating uniformity. Experiments were conducted to investigate the processing parameters and printability. At microwave radiation temperature 95°C, the extruded ink has a significantly increased storage modulus and presents a stable and continuous cylindrical gelatinous state. Filaments can be deposited with high-quality at screw rotary speed 70 rpm and printing speed 5 mm/s. The printed sample demonstrates the excellent printability of multiple layers of extruded ink.

What problem does this paper attempt to address?

### What problem does this paper attempt to solve? This paper aims to solve the problem of poor shape retention of epoxy resin ink during 3D printing due to its low viscosity and slow curing speed. Specifically, the researchers developed a microwave - assisted 3D printer based on the rectangular waveguide (RWG) to overcome these challenges. #### Main problems: 1. **Low viscosity**: Pure epoxy resin ink is prone to spreading and collapsing during the deposition process, affecting the 3D printing quality. 2. **Slow curing speed**: Under traditional methods, the curing speed of epoxy resin is slow, resulting in insufficient shape - retaining ability. 3. **Limitations of existing solutions**: - Adding rheological modifiers (such as fumed silica, nano - clay) will increase the viscosity, hinder the addition and dispersion of other functional fillers, and make the ink difficult to extrude. - When using external energy (such as near - infrared laser, ultraviolet light) for curing, there are problems such as limited curing depth and the need for special curing agents. #### Solutions: - **Microwave - assisted 3D printing**: By synchronizing microwave radiation and ink extrusion, rapid curing is achieved and the shape - retaining ability is improved. - **Optimizing the rectangular waveguide design**: Using multi - physics simulation to determine the key structural parameters of the RWG to ensure good matching of the microwave system and uniform heating of the ink. #### Experimental verification: - **The influence of temperature on the curing behavior**: Through experiments, the influence of the microwave radiation temperature on the curing behavior of the epoxy resin ink was determined, and the optimal temperature range (95 °C) was found. At this temperature, the extruded ink exhibits a stable cylindrical shape and good shape - retaining ability. - **Optimization of printing parameters**: The influence of different printing parameters (such as screw rotation speed, printing speed) on the printing quality was studied, and the optimal parameter combination was determined. ### Formula summary: - **Maxwell's equations** (used to analyze the electric field distribution in the rectangular waveguide): \[ \nabla\times\left(\mu_r^{-1}\nabla\times\vec{E}\right)-\frac{\omega^2}{c^2}(\epsilon' - i\epsilon'')\vec{E}=0 \] where: - \(\vec{E}\) is the electric field strength (V/m) - \(\omega\) is the angular frequency (\(2\pi f\), rad/s) - \(c\) is the speed of light in vacuum (\(3\times 10^8\) m/s) - \(\mu_r\) is the relative permeability - \(\epsilon'\) and \(\epsilon''\) are the real and imaginary parts of the complex permittivity respectively - **Electromagnetic heat generation term**: \[ Q_v=\sigma|\vec{E}|^2\frac{2\pi\epsilon''f}{\epsilon_0} \] where: - \(Q_v\) is the electromagnetic heat generation term (W/m³) - \(\sigma\) is the electrical conductivity (S/m) - \(\epsilon_0\) is the permittivity of free space (\(8.854\times 10^{-12}\) F/m) - **Heat transfer equation**: \[ \rho C_p\frac{\partial T}{\partial t}+\rho C_p\vec{u}\cdot\nabla T+\nabla\cdot(-k\nabla T)=Q_v \] where: - \(\rho\) is the density (kg/m³) - \(C_p\) is the specific heat capacity (J/(kg·K)) - \(\vec{u}\) is the velocity vector (m/s) - \(k\) is the thermal conductivity (W/(m·K)) - \(T\) is the absolute temperature (K) Through these methods and formulas, the researchers successfully solved the shape - retaining problem of epoxy resin ink in 3D printing, providing a new way for efficient and high - quality manufacturing of complex structures.

Microwave-assisted 3D printing of epoxy resin ink using rectangular waveguide

Fabrication of tough epoxy with shape memory effects by UV-assisted direct-ink write printing

Printing Depth Modeling, Printing Process Quantification and Quick-Decision of Printing Parameters in Micro-Vat Polymerization

High-Speed 3D Printing of High-Performance Thermosetting Polymers via Two-Stage Curing

Vat Photopolymerization Bioprinting with a Dynamic Support Bath

3D printing of thermosets with diverse rheological and functional applicabilities

Direct-Writable and Thermally One-Step Curable "Water-Stained" Epoxy Composite Inks

Numerical Model of Jet Formation During Melt Electrowriting for Fabrication of Precise Structures

Additive manufacturing of nanotube-loaded thermosets via direct ink writing and radio-frequency heating and curing

Formability of Printing Ink for Melt Electrowriting

Unstructured Direct Ink Write 3D Printing of Functional Structures with Ambient Temperature Curing Dual‐Network Thermoset Ink

Laser‐Assisted Direct Ink Writing for High‐Fidelity Fabrication of Elastomeric Complex Structures

On the cogent formulation of an elastomeric silicone ink material for direct ink write (DIW) 3D printing

3D Printing by Multiphase Silicone/Water Capillary Inks

Embedded 3D Printing of Architected Ceramics via Microwave‐activated Polymerization

Embedded 3D printing of UV-curable thermosetting composites with continuous fiber

3D printing of multi-scalable structures via high penetration near-infrared photopolymerization

Vapor-induced phase-separation-enabled versatile direct ink writing

Rapid Manufacturing via Selective Radio‐Frequency Heating and Curing of Thermosetting Resins

Fabrication of High Permittivity Resin Composite for Vat Photopolymerization 3D Printing: Morphology, Thermal, Dynamic Mechanical and Dielectric Properties

3D Inkjet Printing of Biomaterials with Solvent‐Free, Thiol‐Yne‐Based Photocurable Inks