Abstract:The aim of this study was to investigate the physical, mechanical, morphological, structural, and thermal properties of polylactic acid (PLA) and polyhydroxybutyrate (PHB) biopolymer composites reinforced with thermally treated wood flour and to determine the formulations having optimum properties by using multi-criteria decision-making (MCDM) methods. As a filler, Scots pine wood flour (untreated and thermally treated at 212 °C) was used at the loading rates of 10% and 30%. The samples were prepared using a twin-screw extruder and then by compression molding. The results showed that the addition of both thermally treated and untreated wood flour slightly increased the density of the composites. According to the color measurement, the thermally treated wood composites were slightly darkened in appearance. In the composites, with both wood fillers, the water absorption and thickness swelling ratios had increased during the 20–250 days of water exposure. Lower water absorption and thickness swelling rates were found for the composites with thermally treated wood filler compared to the other composites. The wood fillers generally lowered the mechanical properties of the PLA and PLA/PHB composites, with the PHB composites as the exception. However, the tensile modulus and Izod impact strength of the composites generally increased with the addition of wood fillers. Morphological examination performed by scanning electron microscopy (SEM) indicated that the wood flour was mostly homogeneously distributed in the matrix, which improved the mechanical properties of the composites. Thermogravimetric analysis (TGA) showed that the addition of wood filler to the neat biopolymers as a rule did not provide significant improvement in the thermal stability; however, the fillers increased the thermal stability of neat PHB. The Fourier-transform infrared (FTIR) spectroscopy detected no differences in the chemical structure of the composites. The X-ray diffraction (XRD) results indicated a general increase in the crystallinity with the addition of wood fillers to the neat biopolymers and the blends. All the findings were subjected to MCDM analysis to determine the formulation having the optimum properties and the results showed this to be the neat PLA sample.

Development of polylactic acid‐untreated bamboo filler composite and its chemical and mechanical properties

Influence of Hot Press Molding Parameters on the Tensile Strength of Bamboo Fiber/PLA Composites

Poly(Lactic Acid) Biocomposites Reinforced With Ultrafine Bamboo-Char: Morphology, Mechanical, Thermal, And Water Absorption Properties

Crystallization behavior and mechanical properties of bio-based green composites based on poly(L-lactide) and kenaf fiber

Improved properties of PLA biocomposites toughened with bamboo cellulose nanowhiskers through silane modification

Nonisothermal Crystallization Behavior of Biocomposites from Poly(lactic Acid) and Bamboo Fiber

Effects of Bamboo Cellulose Nanowhisker Content on the Morphology, Crystallization, Mechanical, and Thermal Properties of PLA Matrix Biocomposites

Effect of Low‐concentration Alkali Solution Pretreatment on the Properties of Bamboo Particles Reinforced Poly(lactic Acid) Composites

Polypropylene biocomposites reinforced with bamboo particles and ultrafine bamboo-char: The effect of blending ratio

Preparation and Characterization of Maleic Anhydride Compatibilized Poly(lactic acid)/Bamboo Particles Biocomposites

Wood Flour-Reinforced Green Composites: Parameter Optimization via Multi-criteria Decision-Making Methods

Poly(l-lactide)/poly(d-lactide)/bamboo fiber (BF) bio-composites with enhanced heat resistance, mechanical and rheological performance

Preparation and Characterization of Polylactic Acid/Bamboo Fiber Composites.

Characterizations of poly-lactic acid/polypropylene filled with bamboo charcoal powder

Reinforcement of Polylactic Acid for Fused Deposition Modeling Process with Nano Particles Treated Bamboo Powder

Fiber treatment impact on toughness and interfacial bonding in epoxidized soya bean oil compatibilized PLA/PBAT bamboo fiber composites

Mechanical and thermal properties of bamboo fiber reinforced polypropylene/polylactic acid composites for 3D printing

Mechanical and Thermal Properties of Bamboo Fiber–Reinforced PLA Polymer Composites: A Critical Study

Sustainable improvement in the polylactic acid properties of 3D printing filaments: The role of bamboo fiber and epoxidized soybean oil‐branched cardanol ether compatibilizer

Excellent mechanical and chemical resistance properties exhibited by bamboo fiber reinforced poly(lactic acid) - epoxy composites

Influence of surface treatments and addition of a reactive agent on the properties of PLA/flax and PLA/bamboo composites