Investigation of the mechanical and thermal properties of epoxy adhesives reinforced by carbon nanotubes and silicon dioxide nanoparticles in single-lap joints
Mürsel Ekrem Murat Koyunbakan Bayram Ünal a Mechanical Engineering,Necmettin Erbakan University,Konya,Türkiyeb Advances Technologies Department,Kütahya Dumlupınar University,Kütahya,Türkiyec Department of Metallurgical and Materials Engineering,Istanbul University-Cerrahpaşa,Istanbul,Türkiye
DOI: https://doi.org/10.1080/01694243.2024.2358037
IF: 2.431
2024-06-04
Journal of Adhesion Science and Technology
Abstract:In this study, the shear strength and thermal properties of the adhesively bonded joints were investigated of adhesives reinforced with nanoparticles using carbon fiber-reinforced composite materials. The diglycidyl ether bisphenol A (DGEBA) was used as the epoxy resin. Single lap joint tests of 1% wt. Multi-walled carbon nanotubes (MWCNT) and 3, 5, and 7% wt. silicon dioxide (SiO 2 ) nanoparticle-reinforced mixed adhesives were performed according to ASTM D5868 standards. The shear strengths of the mixed adhesives obtained by mixing at different ratios were compared with the epoxy resin. Upon conducting an analysis of the shear strengths of nanomaterials, results indicate that the incorporation of 1CNT + 3SiO 2 in the nanomaterials showed the greatest improvement, with a 46% increase in shear strength. 1CNT + 5SiO 2 , 1CNT, and 1CNT + 7SiO 2 showed increases of 32%, 14%, and 5%, respectively. The results of a tensile test indicate that pure epoxy exhibited a tensile strength of 5953 N, 1CNT, and 3SiO 2 , while the epoxy composite demonstrated a significantly higher tensile strength of 8738 N, along with an elongation of 0.72 mm. In addition, the morphology of fractured surfaces was examined by scanning electron microscopy (SEM). To investigate damage mechanisms, such as bridging, crack blunting, and branching of nanoparticles were observed. Characterization of epoxy resin and mixed MWCNT + SiO 2 nanoparticles reinforced adhesives were also performed using Fourier infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and differential thermal analysis (DTA). Nanoparticles are settled between polymer chains, improving polymer chains' motion and thermal properties.
materials science, multidisciplinary,engineering, chemical,mechanics