Unprecedented High-Modulus High-Strength Tapes and Films of Ultrahigh Molecular Weight Polyethylene Via Solvent-Free Route
Sanjay Rastogi,Yefeng Yao,Sara Ronca,Johan Bos,Joris van der Eem
DOI: https://doi.org/10.1021/ma200667m
IF: 5.5
2011-01-01
Macromolecules
Abstract:The ease in processability of synthetic polymers has led to their fast growth as commodity as well as engineering plastic, whereas the latter are used in case of demanding applications.Among several, the most well-studied polymer is probably polyethylene.This polymer, based on a simple À(CH 2 ÀCH 2 )À repeating unit, can be used for day-to-day applications as well as for more challenging duties such as prostheses, soft and hard ballistics, light weighted ropes, etc.The wide range of physical and mechanical properties is accessible due to fine control of the molecular architecture, coming from the better understanding of polymer synthesis.The development of a material with the desired properties requires the combination of several disciplines in science, including chemistry, physics, rheology, and processing.It is recognized that, for linear polyethylene, virtually free of chain branching, the physical properties such as wear, abrasion resistance, and impact strength enhance with increasing molar mass.However, the material becomes more difficult to process because the zero shear viscosity follows the well-known power law η 0 µ M 3.4 , thus making the polymer having weight-average molar mass greater than 1 million g/mol nearly impossible to process via the conventional processing route. 1,2The cause for the increase in viscosity, when increasing the molar mass of the polymer, is related to the increasing number of physical entanglement (friction points due to contact of chain segments) as the molar mass between the entanglement, M e , is considered to be a constant for a given polymer.For example, in the case of linear polyethylene, the molar mass between entanglement is ∼1200 g/mol. 3number of entanglement per chain can be effectively suppressed by dissolution of the polymer in a suitable solvent.In dilute solutions, below the so-called overlap concentration Φ*, the number of entanglement per chain can be reduced considerably. 4In the case of crystallizable polymers, such as linear polyethylene, the reduced entanglement density in the solution can be made permanent since the long chain molecules form folded-chain crystals on cooling where entanglement reside in the amorphous phase, a well-studied phenomenon in polymer physics. 5,6The reduction of entanglement in the amorphous region of the semicrystalline polymer favor the postdrawing process. 7Following these concepts, the existing commercial route has been adopted to develop high-modulus high-strength 50 fibers, where dissolution of less than 6 wt % of the ultrahigh 51 molecular weight polymer in a high boiling point solvent such as 52 decalin 8 is required.Prior to removal of the 94 wt % of the 53 solvent, the solution is cooled for crystallization.The disen-54 tangled solid state thus achieved is used for its ease in drawability 55 to make high-modulus high-strength fibers.However, on heating 56 the solution crystallized polymer, the disentangled chains tend to 57 re-entangle, erasing the disentangled state. 9,1058 A more elegant and also technologically more advanced way to 59 generate disentangled linear polyethylene crystals is via direct 60 polymerization in the reactor.11À13 At low polymerization tem-61 peratures and low catalyst activity/concentration, individual 62 growing chains will form their own folded chain crystals.In the 63 limiting case where the growing chains are separated far enough 64 from each other, ultimately monomolecular crystals can be 65 formed.If completely disentangled PE structures can be obtained 66 via solution-crystallization and/or via direct controlled synthesis, 67 the intriguing question is whether this disentangled state will be 68 preserved upon melting and what is the time scale to generate a 69 fully entangled equilibrium polymer melt.Some of these funda-70 mental questions have been addressed previously.14À18 71 The deformation behavior in the solid-state processing (free 72 of solvent), either uniaxial or biaxial, is likely to be strongly 73 dependent on the topological constraints that are established in 74 the amorphous region of the polymer.Thus, in this publication 75 with the help of solid-state NMR studies we have followed 76 differences between the amorphous regions of the nascent 77 entangled and the nascent disentangled polyethylenes synthe-78 sized via the conventional ZieglerÀNatta (ZÀN) and the direct 79 controlled synthesis, respectively.Uniaxial and biaxial deforma-80 tion aspects of the disentangled polyethylene have been com-81 pared with the entangled polyethylene.Resultant properties of 82 the two materials against the draw ratio have been investigated.83 Crystallinity measurements and the resultant tensile properties in 84 the drawn tapes have been investigated by solid-state NMR.With 85 the help of X-ray diffraction studies, the cause of the high 86 modulus in the solid-state processed materials has been com-87 pared with the polyethylene processed via the solution route.