Abstract:The components made out of hypereutectic high-chromium cast iron (HCCI), featured with high abrasion resistance and hardness, are usually subjected to destabilization treatment before use, to improve their hardness and wear resistance by destabilizing the retained austenite which transforms to martensite. This study investigates the effects of destabilization and tempering heat treatment on the microstructure and mechanical properties of an HCCI with and without modification of primary carbides. For the unmodified HCCI, the destabilization simultaneously increased both hardness and the transverse rupture strength (TRS). Increasing the destabilization temperature from 970 to 1090 °C led to a marginal decrease in hardness and slight increase in TRS. Destabilization at 1090 °C increased the transverse rupture strength (TRS) by 54% compared to the as-cast HCCI without reduction in wear resistance due to the coarsening of the secondary carbides. In addition, tempering within a temperature range from 200 to 280 °C after destabilization at 1090 °C led to a slight decrease in hardness, but an increase in TRS and wear resistance. Further increasing the tempering temperature to 310, 340 and 400 °C did not vary the properties. Tempering at 280 °C after destabilization at 1090 °C enabled more than 85% increase in TRS compared to the as-cast HCCI. The influence of destabilization temperature on the TiB 2 -modified HCCI is similar to the unmodified alloy. But, tempering after destabilization at 1090 °C decreased both hardness and TRS without significant variation of wear resistance even though a TRS peak was obtained at 310 °C tempering. Hence, to achieve the best performance an optimized heat treatment for the unmodified HCCI is destabilization at 1090 °C followed by tempering at 280 °C. For the TiB 2 -modified HCCI, tempering is not needed. Rationalizations of the mechanical properties are also discussed in terms of microstructure.

Effect of TiB2 addition on microstructure and mechanical properties of a hypereutectic high chromium cast iron

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Effect of TiC Particle Additions on Structure and Properties of Hypereutectic High Chromium Cast Iron

Effect of titanium on the microstructure of hypereutectic high-chromium cast iron

Effect of Ti Addition on Morphology and Size of Primary M7c3 Type Carbide in Hypereutectic High Chromium Cast Iron

Effect of Titanium on the As-Cast Microstructure of Hypereutectic High Chromium Cast Iron

Effect of Titanium on the Morphology of Primary M7C3 Carbides in Hypereutectic High Chromium White Iron

Effect of Multi-Element Microalloying on the Structure and Properties of High Chromium Cast Iron

Refinement of primary carbides in hypereutectic high-chromium cast irons: a review

Effects of destabilization and tempering on microstructure and mechanical properties of a hypereutectic high-chromium cast iron

Refining Mechanism of Ti on Hypereutectic High-Chromium Cast Iron

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Ti-bearing Hypereutectic High Chromium White Cast Iron

Effect of TiB2 addition on microstructure and fluidity of cast TiAl alloy

Effect of (nbti)c Particles on the Microstructure and Hardness of High Chromium and Nickel Indefinite Chilled Cast Iron

Effect of TiC Addition on the High-Temperature Hardness and the Carbide Stability in Al0.2CoCrFeNi1.5Ti High-Entropy Alloy

Enhanced combination of strength and ductility in the semi-solid rheocast hypereutectic Al Si alloy with the effect of in-situ TiB2 particles

Microstructure features and mechanical properties of non-heat treated HPDC Al9Si0.6Mn–TiB 2 alloys

Microstructure Features and Mechanical Properties of Non-Heat Treated HPDC Al9Si0.6Mn–TiB2 Alloys

The effect of TiC on microstructure and mechanical properties of Ti-5553 beta phase titanium alloy

Microstructure and high-temperature wear properties of in situ TiC composite coatings by plasma transferred arc surface alloying on gray cast iron

Improving impact toughness of a high chromium cast iron regarding joint additive of nitrogen and titanium