Abstract:The work aims to improve dry tribological property of high speed steel and study influence of different Ti content on tribological property of graphite-like carbon films. Graphite-like carbon films of different Ti content were fabricated with unbalanced magnetron sputtering ion plating technology. Microstructures and mechanical properties of the films were characte-rized with optical microscope, scanning electron microscopy, Raman spectrometer, Rockwell hardness tester and nanoindentor. Dry tribological properties of the films were detected with high-speed linear reciprocating abrasion testing machine. Grinding cracks were observed with optical microscopy. The prepared carbon film surface particles were in small size, the cross section was compact and tended to be columnar structure. With the increase of Ti target sputtering current, the increasing Ti element in-terrupted growth of sp3 bond, leading to the generation of more stable sp2 bond. The sp2 bond content first increased and then decreased, reaching the maximum at 0.8 A. At the current of 1.1 A, Ti content reached the maximum, both the sp2 bond and sp3 bond decreased. Adherence between the carbon film and substrate first increased and then decreased as Ti target current in-creased, reaching the optimum value (of about grade HF3) at 0.8 A. Hardness and elastic modulus first decreased and then in-creased, reaching the minimum at 0.8 A. Friction coefficient of the carbon films was lower than that of M42, ranging from 0.09 to 0.12. Wear rate first increased and then decreased, maintaining at nearly (5~15)×10?16 m3/(N·m). Graphite-like carbon films of different Ti content can reduce adhesive wear caused by mutual abrasion between high speed steel and steel ball significantly, therefore decreasing the friction coefficient and wear rate.

Influence of titanium concentration on mechanical properties and wear resistance to Ti6Al4V of Ti-C:H on cemented carbide

Influence of Carbon Contents on the Structure and Tribocorrosion Properties of Tisicn Coatings on Ti6al4v

Effect of titanium content on wear resistance of CoCuFeNiVTix high-entropy alloys

Mechanical and tribological properties of TiC/amorphous hydrogenated carbon composite coatings fabricated by DC magnetron sputtering with and without sample bias

Effects of Ti Content on Microstructure, Mechanical and Tribological Properties of Ti-doped Amorphous Carbon Multilayer Films

Influences of different temperatures on the mechanical properties and wear resistance against Ti6Al4V of Ti doped diamond-like carbon deposited on cemented carbide

Effects of Al Incorporation on the Mechanical and Tribological Properties of Ti-doped A-C:H Films Deposited by Magnetron Sputtering

Microstructure, Tribological and Cutting Performance of Ti-DLC/α-C:H Multilayer Film on Cemented Carbide

Tuning composition and microstructure by doping Ti and C for enhancing mechanical property and wear resistance of Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloy matrix composites

Dry Friction and Wear Properties of Graphite-like Carbon Films of Different Ti Content

Analysis on the Wear Performances of Cemented Carbide Tools Containing Ti in the Coatings When Machining Ti-6Al-4V Alloys

The Electrochemical and Mechanical Properties of Ti Incorporated Amorphous Carbon Films in Hanks' Solution

The Tribological Performance of Surface Treated Ti6A14V as Sliding Against Si3N4 Ball and 316L Stainless Steel Cylinder

Microstructure and Tribological Properties of Ti-contained Amorphous Carbon Film Deposited by DC Magnetron Sputtering

Effect of carbon content on the tribological behaviour of TiC x coatings prepared by reactive HiPIMS

Effects of C content on the microstructure, mechanical and tribological properties of TiAlSiCN coatings

Wear Behavior of Ti6Al4V Based Hybrid Composites Reinforced with TiB2(7.5%) + TiC (7.5%)

Influence of Al/Ti Atomic Ratio on Hard Al–TiCN Films

Effect of C doping on structure and properties of TiAlCrN coatings by filter cathode vacuum arc deposition

The Effect of Carbon Doping on Microstructure, Mechanical Properties, Wear Resistance and Cutting Performance of AlTiCN Coating

Microstructure and tribological behaviors of laser cladded CuAlMnTi–xTiC composite coatings at elevated temperature