Effects of Calcination Temperature on the Synthesis of One-Pot Sol-Gelled Barium Titanate Powder and Its Performance as an Endodontic Radiopacifier

Pei-Jung Chang,May-Show Chen,Chi-Han Cheng,Yuh-Jing Chiou,Chin-Yi Chen,Cherng-Yuh Su,Chung-Kwei Lin

DOI: https://doi.org/10.3390/ma17112701

IF: 3.4

2024-06-04

Materials

Abstract:Barium titanate (BaTiO3, BTO), conventionally used for dielectric and ferroelectric applications, has been assessed for biomedical applications, such as its utilization as a radiopacifier in mineral trioxide aggregates (MTA) for endodontic treatment. In the present study, BTO powders were prepared using the sol-gel process, followed by calcination at 400–1100 °C. The X-ray diffraction technique was then used to examine the as-prepared powders to elucidate the effect of calcination on the phase composition and crystalline size of BTO. Calcined BTO powders were then used as radiopacifiers for MTA. MTA-like cements were investigated to determine the optimal calcination temperature based on the radiopacity and diametral tensile strength (DTS). The experimental results showed that the formation of BTO phase was observed after calcination at temperatures of 600 °C and above. The calcined powders were a mixture of BaTiO3 phase with residual BaCO3 and/or Ba2TiO4 phases. The performance of MTA-like cements with BTO addition increased with increasing calcination temperature up to 1000 °C. The radiopacity, however, decreased after 7 days of simulated oral environmental storage, whereas an increase in DTS was observed. Optimal MTA-like cement was obtained by adding 40 wt.% 1000 °C-calcined BTO powder, with its resulting radiopacity and DTS at 4.83 ± 0.61 mmAl and 2.86 ± 0.33 MPa, respectively. After 7 days, the radiopacity decreased slightly to 4.69 ± 0.51 mmAl, accompanied by an increase in DTS to 3.13 ± 0.70 MPa. The optimal cement was biocompatible and verified using MG 63 and L929 cell lines, which exhibited cell viability higher than 95%.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

The problem this paper attempts to address is the evaluation of the suitability of barium titanate (BaTiO3, BTO) powders, prepared via a one-pot sol-gel method, as radiopacifiers in mineral trioxide aggregate (MTA) for dental materials by studying the effect of calcination temperature on their properties. Specifically, the paper investigates the phase composition and grain size changes of BTO powders at different calcination temperatures and their impact on the radiopacity and radial tensile strength of MTA-like cements. The aim is to determine the optimal calcination temperature to produce BTO-added MTA-like cements with the best performance. Additionally, the paper evaluates the biocompatibility of this optimized BTO-added MTA-like cement to ensure its safety in practical applications.

The research background of the paper includes the extensive use of BTO in traditional electronic applications and its potential applications in the biomedical field in recent years, particularly as a radiopacifier in MTA. Traditional MTA, although widely used in dental treatments, has drawbacks such as handling difficulties, long setting times, insufficient mechanical strength, cytotoxicity, and tooth discoloration. Therefore, finding a new radiopacifier that can improve these properties has become a research focus. By adjusting the preparation process of BTO, especially the calcination temperature, the physicochemical properties of BTO can be significantly influenced, thereby affecting its effectiveness as a radiopacifier in MTA.