Structure and properties of titanium-aluminum alloys doped with niobium and tantalum
A. A. Bondar,V. T. Witusiewicz,U. Hecht,M. V. Remez,V. M. Voblikov,N. I. Tsyganenko,Ya. I. Yevich,Yu. M. Podrezov,T. Ya. Velikanova
DOI: https://doi.org/10.1007/s11106-011-9345-6
2011-10-01
Powder Metallurgy and Metal Ceramics
Abstract:Ternary as-cast Ti55−xNbxAl45, Ti53−xNbxAl47, Ti55−xTaxAl45, and Ti53−xTaxAl47 alloys, where x = 0, 4, 8, and 12, and Ti45Nb8−xTaxAl47 and Ti47Nb8−xTaxAl45 quaternary alloys, where x = 2, 4, and 6, melted in a laboratory arc furnace from pure components (~99.9 wt.%) are studied by X-ray diffraction (XRD), scanning and transmission electron microscopy (SEM and TEM), differential thermal analysis (DTA), and compression testing. The alloys are found to consist mainly of a superfine lamellar structure of decomposition β → α → α + γ → α2+ γ and contain tiny islands of the γ phase and also the β phase at 12 at.% Nb or Ta. The CALPHAD approach is used to obtain a thermodynamic description of the Al − Nb − Ta − Ti system, which adequately reproduces the experimental data. The compression tests performed at room temperature show that the ternary alloys with 45 at.% Al are characterized by higher strength but lower plasticity than the alloys with 47 at.% Al. For the Ti46Nb8Al46 and Ti46Ta8Al46 alloys, high strength in the temperature range 20 – 800°C and a drop in plasticity to 2 – 4% at 200 – 600°C are revealed. Among the quaternary alloys examined, the best combination of strength and plasticity (σ02 = 1043 MPa, σult = 1612 MPa, εpl = 12.4%) is exhibited by the Ti47Nb4Ta4Al45 alloy.
metallurgy & metallurgical engineering,materials science, ceramics