Effect of high and low Nb content in multicomponent Nb–Ni–Ti–Zr–Co alloy on its structure, hardness and hydrogen permeability

E.B. Kashkarov,L.A. Svyatkin,K.S. Gusev,S.O. Ognev,M. Koptsev,D.V. Terenteva

DOI: https://doi.org/10.1016/j.intermet.2023.108180

IF: 4.075

2024-01-05

Intermetallics

Abstract:In the present work, novel multicomponent Nb–Ni–Ti–Zr–Co alloys were synthesized by arc melting. Two alloys with low and high Nb contents and an equimolar high-entropy alloy (HEA) were produced and compared. The influence of the elemental composition on their microstructure, phase composition, lattice constants, hardness and hydrogen permeability was investigated. The synthesized Nb–Ni–Ti–Zr–Co alloys are characterized by near-equimolar BCC-(Nb, Ni, Ti, Zr, Co) and Nb-rich BCC-Nb(Ni, Ti, Zr, Co) phases. The equimolar Nb 20 Ni 20 Ti 20 Zr 20 Co 20 alloy had the highest concentration of BCC-(Nb, Ni, Ti, Zr, Co) phase (84 vol %), while the Nb 74 Ni 6 Ti 9 Zr 5 Co 6 alloy had the highest concentration of Nb-rich BCC phase (95 vol %). First-principles study of the lattice parameters for the Nb–Ni–Ti–Zr–Co alloy revealed that the lattice parameter of the BCC phase decreases with Ni and Co addition and increases with Nb, Zr addition. Titanium does not significantly affect the lattice constant of BCC phase for compositions close to equimolar (10–30 at. %). The microhardness of the alloys decreases with increasing Nb content, which is mainly due to the proportion of softer Nb-rich BCC phase and microstructural changes. The synthesized Nb 15 Ni 20 Ti 15 Zr 30 Co 20 and Nb 20 Ni 20 Ti 20 Zr 20 Co 20 alloys demonstrate high hydrogen permeability at 400 °C that makes them promising for hydrogen purification membranes. It is shown high-entropy Nb 20 Ni 20 Ti 20 Zr 20 Co 20 alloy exhibit highest resistance to hydrogen embrittlement, while high Nb content alloys are strongly susceptible to embrittlement.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering