Abstract:Basalt fiber (BF) and nano-silica (NS) are used to improve the properties of recycled aggregate concrete (RAC) and produce modified RAC (MRAC). The fatigue failure patterns of the MRAC were observed through a uniaxial compression fatigue test, and the reasons for the different patterns were explained. The effects of the stress level, replacement rate, and loading frequency on the fatigue life were investigated, and the effects of BF and NS on the fatigue strain, damage evolution, and energy dissipation evolution of MRAC were analyzed. The enhancement mechanism of BF and NS on RAC was revealed using microstructural analysis techniques, such as scanning electron microscopy (SEM) and computed tomography (CT). The results showed that the fatigue failure modes of the MRAC could be divided into split, shear, and mixed failures. The fatigue life and fatigue strain of RAC exhibited a pattern of initially increasing and subsequently decreasing with an increase in the BF content (from 0 kg m −3 to 3 kg m −3 and then to 6 kg m −3 ). At stress level of 0.80, the average fatigue life of the specimens increased by 76.15 % compared to RAC when the BF doping was 3 kg m −3 ; however, when the BF doping was increased to 6 kg m −3 , the average fatigue life of the specimens increased by only 47.68 % compared to RAC. The mixed BF and NS improved the fatigue life of RAC more than the single mixed BF or NS. Fatigue equations and unified single logarithmic fatigue equations, including fiber parameters, were established to accurately describe the relationship between the fatigue stress level, fatigue life, and failure probability. The fatigue strain gradually decreases with increasing NS content (0–2 %); with increasing loading frequency (from 1 Hz to 10 Hz and then to 15 Hz), the fatigue strain gradually decreases. The fatigue life of the MRAC decreased dramatically at low loading frequencies (1 Hz) and then steadily increased as the loading frequency increased. BF and NS have an improving effect on the porosity of microstructure, improve the fatigue life of RAC, and BF exhibits a more significant improvement than NS. A composite fatigue damage model that comprehensively considers the contribution rates of NS and BF was established, and the fatigue damage evolution of the MRAC was predicted.

Macro-mechanical properties and fine scale damage mechanism of carbon fiber-modified recycled coarse aggregate concrete under sodium sulfate-dry-wet and freeze-thaw cycling coupling effects

Flexural Behavior and Durability Properties of Recycled Aggregate Concrete (RAC) Beams Subjected to Long-Term Loading and Chloride Attacks

Characterizations and Quantification of Freeze-Thaw Behaviors of Recycled Brick Aggregate Concrete

Coupled Effects of the Freeze-Thaw Cycles and Salt Erosion on the Performance of Recycled Aggregate Concrete

Experimental investigation on the flexural performance and damage process of steel fiber reinforced recycled coarse aggregate concrete

Study on compressive mechanical properties of recycled aggregate concrete with silica fume at different strain rates

Fatigue damage evolution of modified recycled aggregate concrete

Study on stress–strain relationship and constitutive model of recycled aggregate concrete under axial cyclic compression

Durability analysis of metakaolin recycled concrete under sulphate dry and wet cycle

Salt frost damage evolution and transport properties of recycled aggregate concrete under sustained compressive loading

Mechanical Properties of Fibre Reinforced Seawater Sea-Sand Recycled Aggregate Concrete Under Axial Compression

Insight into the Mechanical Properties and Microstructure of Recycled Aggregate Concrete Containing Carbon Fibers and Nano-SiO2

Study on the Mechanical Properties and Microstructure of Fiber-Reinforced Concrete Subjected to Sulfate Erosion

Investigation of the macro performance, mechanism, and durability of multiscale steel fiber reinforced low-carbon ecological UHPC

Acoustic emission behavior and damage evaluation of recycled aggregate concrete under compression

Grey entropy analysis of strength and void structure of carbon nanotubes concrete under the coupling of sulfate attack and freeze-thaw cycles

Investigation on Mechanical and Microstructure Properties of Steel Fiber Reinforced Concrete

Fracture Mechanical Properties of Steel Fiber Reinforced Self-Compacting Concrete under Dry–Wet Cycle Sulfate Attack

The Influence of Freeze–Thaw Cycles and Corrosion on Reinforced Concrete and the Relationship between the Evolutions of the Microstructure and Mechanical Properties

Improving the salt frost resistance of recycled aggregate concrete modified by air-entraining agents and nano-silica under sustained compressive loading

Effect of Sulfate Freeze-Thaw on the Stress-Strain Relationship of Recycled Coarse Aggregate Self-Compacting Concrete: Experimental and Machine Learning Algorithms