Abstract:Developing a high-strength, flame-resistant structural material derived from wood is desirable for advanced applications in the transportation, construction, automotive, and aerospace sectors. Here, a low-cost and high-efficiency top-down method was designed for processing natural wood veneers into lightweight yet strong bulk structural wood-based composites. The composites were produced using delignified wood veneers as a continuous reinforcing material and epoxy resin as the adhesive, followed by hot pressing. Densification of the veneers and good adhesion among the veneers played a pivotal role in the mechanical performance of the composites. A record-high flexural strength of 436.1 MPa and a toughness of 12.3 MJ·m–3 were achieved. Furthermore, the low density of the wood composite led to a specific flexural strength of 323.0 MPa·cm3·g–1, which is significantly greater than those reported for other wood-based composites and some metal materials (e.g., steels and alloys). We also explored the feasibility of using the composite in unmanned drones. In addition, the delignified wood veneers were infiltrated with 1.5% ammonium polyphosphate (APP), which improved the fire-retardant and self-extinguishing properties of the composites. This work demonstrates that high-strength wood products exhibit significant potential in many applications.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.0c09390.Molding process of DWLC-41.4% with different shapes (Figure S1); delignified wood panels with different lignin removal contents (Figure S2); thickness swelling (24 h) (Figure S3); SEM images of DWLC-0%, DWLC-23.2%, and DWLC-55.1% (Figure S4); micro-CT images (Figure S5); tensile and flexural strength of DWLC-41.4% with and without epoxy resin (Figure S6); photographs of wood veneer pull-out tests: before (left) and after (right) (Figure S7); bonding strength of wood veneer and epoxy resin (Figure S8); microstructure of fracture surfaces of pure epoxy resin (Figure S9); compressive strength of natural birch wood and DWLC-41.4% (Figure S10); mechanical properties and microstructures of DWLCs with and without flame retardant (Figure S11); TG curves of DWLC, 1.5% APP/DWLC, and 2.5% APP/DWLC (Figure S12); mass loss of DWLC, 1.5% APP/DWLC, and 2.5% APP/DWLC after the cone test (Figure S13); TSR curves of DWLC, 1.5% APP/DWLC, and 2.5% APP/DWLC (Figure S14); XPS spectra of P of 1.5% APP/DWLC and 2.5% APP/DWLC (Figure S15); comparison of TTI between DWLC-41.4% and other wood-based composites (Table S1); and XPS analysis of the external char of DWLC-41.4% with and without flame retardant (Table S2) (PDF)Takeoff process of an unmanned drone (Movie S1) (MP4)This article has not yet been cited by other publications.

High-Performance All-Bio-Based Laminates Derived from Delignified Wood

Fabrication and Design of Wood-Based High-Performance Composites

Laminating Delignified Wood Veneers toward High-Strength, Flame-Retardant Composites for Structural Applications

Glueless formaldehyde-free biocomposites with high strength based on the three-dimensional structure of wood fibres

Reengineering Wood into a High-Strength, and Light-Weight Bio-Composite Material for Structural Applications

A Strong, Tough and Fire-Retardant Biomimetic Multifunctional Wooden Laminate

High-performance Self-Bonding Bio-Composites from Wood Fibers

Delignified and Densified Cellulose Bulk Materials with Excellent Tensile Properties for Sustainable Engineering

Bio-based composites fabricated from wood fibers through self-bonding technology

Bio-inspired, epoxy-based lamellar composites with superior fracture toughness by delignified wood scaffold

Exploring strategies for valorizing wood processing waste: advancing sustainable, fully lignocellulosic biocomposites

High-Performance Lignocellulosic Self-Bonding Composites via Dialdehyde Modification and Water-Involved Low-Temperature Hot Pressing

Towards high performance wood composites through interface customization with cellulose-based adhesive

Green and sustainable fabrication of DES-pretreated high-strength densified wood

Lightweight, Strong, and Transparent Wood Films Produced by Capillary Driven Self‐Densification

High-Performance, Adhesive-Free, Sustainable Biomass-Based Materials Via a Selective in Situ Oxidation Interface

Sustainable Engineering Polymer Composites Fabricated Using Delignified Bamboo Fiber as Reinforcement and Walnut Shell Powder as Filler

A strong, flame-retardant, and thermally insulating wood laminate

Transparent, UV Blocking, and Strong Wood-Based Biocomposites with Isotropic Optical and Mechanical Properties

Synergistic in-situ reinforcement of lignin and adhesive for high-performance aligned bamboo fibers composites

Stacking self-gluing cellulose II films: A facile strategy for the formation of novel all-cellulose laminates