Laminating Delignified Wood Veneers toward High-Strength, Flame-Retardant Composites for Structural Applications
Qiheng Tang,Miao Zou,Kezheng Gao,Liang Chang,Li Gao,Wenjing Guo
DOI: https://doi.org/10.1021/acssuschemeng.0c09390
2021-07-28
Abstract:Developing a high-strength, flame-resistant structural material derived from wood is desirable for advanced applications in the transportation, construction, automotive, and aerospace sectors. Here, a low-cost and high-efficiency top-down method was designed for processing natural wood veneers into lightweight yet strong bulk structural wood-based composites. The composites were produced using delignified wood veneers as a continuous reinforcing material and epoxy resin as the adhesive, followed by hot pressing. Densification of the veneers and good adhesion among the veneers played a pivotal role in the mechanical performance of the composites. A record-high flexural strength of 436.1 MPa and a toughness of 12.3 MJ·m–3 were achieved. Furthermore, the low density of the wood composite led to a specific flexural strength of 323.0 MPa·cm3·g–1, which is significantly greater than those reported for other wood-based composites and some metal materials (e.g., steels and alloys). We also explored the feasibility of using the composite in unmanned drones. In addition, the delignified wood veneers were infiltrated with 1.5% ammonium polyphosphate (APP), which improved the fire-retardant and self-extinguishing properties of the composites. This work demonstrates that high-strength wood products exhibit significant potential in many applications.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.0c09390.Molding process of DWLC-41.4% with different shapes (Figure S1); delignified wood panels with different lignin removal contents (Figure S2); thickness swelling (24 h) (Figure S3); SEM images of DWLC-0%, DWLC-23.2%, and DWLC-55.1% (Figure S4); micro-CT images (Figure S5); tensile and flexural strength of DWLC-41.4% with and without epoxy resin (Figure S6); photographs of wood veneer pull-out tests: before (left) and after (right) (Figure S7); bonding strength of wood veneer and epoxy resin (Figure S8); microstructure of fracture surfaces of pure epoxy resin (Figure S9); compressive strength of natural birch wood and DWLC-41.4% (Figure S10); mechanical properties and microstructures of DWLCs with and without flame retardant (Figure S11); TG curves of DWLC, 1.5% APP/DWLC, and 2.5% APP/DWLC (Figure S12); mass loss of DWLC, 1.5% APP/DWLC, and 2.5% APP/DWLC after the cone test (Figure S13); TSR curves of DWLC, 1.5% APP/DWLC, and 2.5% APP/DWLC (Figure S14); XPS spectra of P of 1.5% APP/DWLC and 2.5% APP/DWLC (Figure S15); comparison of TTI between DWLC-41.4% and other wood-based composites (Table S1); and XPS analysis of the external char of DWLC-41.4% with and without flame retardant (Table S2) (PDF)Takeoff process of an unmanned drone (Movie S1) (MP4)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology