Abstract:The influence of hydrogen on defect structure in pure titanium was systemically investigated using X-ray diffraction (XRD) and positron annihilation spectroscopy (PAS). The results showed that hydrogen damage was related to hydrogen concentration, and PAS provided a new idea for the study in the formation of hydride and open volume defects. XRD results showed that two types of titanium hydrides were observed in hydrogen-charged samples, i.e., δ-TiHx and ε-TiH2, and the degree of lattice expansion and the content of hydride increased with hydrogen content. The variation of the S parameter and W parameter indicated that a great deal of vacancy-type defects formed during electrochemical hydrogen charging, and hydrogen atoms could combine with vacancy to form a certain amount of hydrogen-vacancy complexes (HnVm), meanwhile, the hydrogen damage varied significantly with depth. The effective open volume of vacancy-type defect increased with hydrogen charging concentration, and hydrogen-vacancy cluster transformed into HnVm (n < m) cluster, vacancy defects were gradually dominated. In addition, According to the different annihilation environment of positron in titanium hydrides and hydrogen-vacancy complexes, the existence of titanium hydrides and the existing form of hydrogen in defect could be identified in Doppler broadening spectroscopy (CDB). This provided a new way to identify the formation of hydrides and to detect the existing form of low concentration hydrogen in samples.

Effect of electrochemical hydrogen charging on defect structure in titanium

Effect of pre-deformation on hydrogen diffusion and hydrogen induced damage in commercially pure titanium

Exploration of vacancy defect formation and evolution in low-energy ion implanted pure titanium

Effect of hydrogen on the structural and phase state and defect structure of titanium alloy

Investigation of the interaction between hydrogen and irradiation defects in titanium by using positron annihilation spectroscopy

In-situ synchrotron based high energy X-ray diffraction study of the deformation mechanism of δ-hydride in a commercially pure titanium

In-situ synchrotron-based high energy X-ray diffraction study of the deformation mechanism of δ-hydrides in a commercially pure titanium

Hydrogen-surface interaction from first-principles calculations and its implication to hydrogen embrittlement mechanisms of titanium

Improving the Mechanical Processing of Titanium by Hydrogen Doping: A First-Principles Study

Effect of Mo alloying on vacancy-defect evolution and irradiation damage in titanium alloy

Hydrogen Diffusion-Induced Crystallographic Changes in Α Plus Β Titanium Alloy

Breaking the continuous hydride network in hydrogen-charged pure titanium to repair hydride–induced performance degradation by applying a pulsed electric current

An Investigation on Structure, Deformation and Fracture of Hydrides in Titanium with a Large Range of Hydrogen Contents

Hydrogen Induced Microstructure Evolution of Titanium Matrix Composites

Hydrogen Impurity Defects in Rutile TiO2

Hydrogen Damage Process of Dual-Phase Ti-6Al-4V Alloy: from Surface Passive Film to the Interior Substrate

Characterizing solute hydrogen and hydrides in pure and alloyed titanium at the atomic scale

Effects of hydrogen charge on the intergranular corrosion of high-defect-density ultrapure ferrite stainless steel

Effect of electrochemical hydrogen charging on the mechanical property and corrosion behavior of Ti-3Mo alloy

Electrochemical Studies on the Ionic Charge Transfer Properties of the Oxygen Vacancy Defects in the Oxide Films Formed on Titanium

Microstructure of Cyclically Deformed Titanium with Low Hydrogen Concentration I. Crystal Rotation and Formation of Cell Structure Near Hydrides