Effect of electrochemical hydrogen charging on defect structure in titanium
Qianqian Wang,Xudong An,Te Zhu,Mingpan Wan,Peng Zhang,Fengjiao Ye,Yamin Song,Chaowen Huang,Rui Ma,Baoyi Wang,Xingzhong Cao
DOI: https://doi.org/10.1016/j.jallcom.2021.160909
IF: 6.2
2021-12-01
Journal of Alloys and Compounds
Abstract:<p>The influence of hydrogen on defect structure in pure titanium was systemically investigated using X-ray diffraction (XRD) and positron annihilation spectroscopy (PAS). The results showed that hydrogen damage was related to hydrogen concentration, and PAS provided a new idea for the study in the formation of hydride and open volume defects. XRD results showed that two types of titanium hydrides were observed in hydrogen-charged samples, i.e., δ-TiH<sub>x</sub> and ε-TiH<sub>2</sub>, and the degree of lattice expansion and the content of hydride increased with hydrogen content. The variation of the S parameter and W parameter indicated that a great deal of vacancy-type defects formed during electrochemical hydrogen charging, and hydrogen atoms could combine with vacancy to form a certain amount of hydrogen-vacancy complexes (H<sub><em>n</em></sub>V<sub><em>m</em></sub>), meanwhile, the hydrogen damage varied significantly with depth. The effective open volume of vacancy-type defect increased with hydrogen charging concentration, and hydrogen-vacancy cluster transformed into H<sub><em>n</em></sub>V<sub><em>m</em></sub> (<em>n</em> < <em>m</em>) cluster, vacancy defects were gradually dominated. In addition, According to the different annihilation environment of positron in titanium hydrides and hydrogen-vacancy complexes, the existence of titanium hydrides and the existing form of hydrogen in defect could be identified in Doppler broadening spectroscopy (CDB). This provided a new way to identify the formation of hydrides and to detect the existing form of low concentration hydrogen in samples.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering