Multiple-Defect Management for Efficient Perovskite Photovoltaics
Xiaoyu Yang,Yue Ni,Yuzhuo Zhang,Yanju Wang,Wenqiang Yang,Deying Luo,Yongguang Tu,Qihuang Gong,Haifeng Yu,Rui Zhu
DOI: https://doi.org/10.1021/acsenergylett.1c01039
IF: 22
2021-06-08
ACS Energy Letters
Abstract:A variety of defects exist on the crystalline surfaces of solution-processed polycrystalline perovskites, resulting in photovoltaic output losses and subsequent degradations. It is necessary to develop a versatile passivator that can concurrently eliminate multiple defects, including vacancy, interstitial, antisite substitution, and dissociative I<sub>2</sub>. Herein, we focus on multiple-defect management to optimize defective perovskite surfaces by using three kinds of chemical bonds with a pyridine-containing polymeric agent. Coordination bonds alleviate the distorted PbI<sub><i>x</i></sub> octahedrons by digesting I vacancies, and hydrogen bonds stabilize ammonium cations to eliminate organic vacancies and deep-level antisite defects. Furthermore, the dissociated I<sub>2</sub> acting as electron traps from the coupled I interstitials could be blocked by supramolecular halogen bonds. Based on the low-defect perovskite films, substantial increases in photovoltaic efficiencies, going up to 22.02% and 23.14%, are achieved in planar and mesoporous devices, respectively, with nonencapsulated cells retaining 90% of their original efficiencies after 2200 h of aging in ambient conditions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsenergylett.1c01039?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsenergylett.1c01039</a>.Supplementary figures, tables, and notes: schematic of the distortion and relaxing of the octahedron (Figure S1); evaluation of supramolecular halogen bonds (Figures S2–S6); crystallographic information (Figure S7); PL information (Figure S8); photovoltaic performance (Figures S9–S11); ratio of current (Figure S12); external resistance by P4VP (Figure S13); XRD evaluation (Figure S14); fitted parameters from TRPL spectra (Table S1); photovoltaic performance (Tables S1–S3); analysis for Jahn–Teller effect (Note S1); space-charge-limited current method (Note S2); microstrain analysis (Note S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.1c01039/suppl_file/nz1c01039_si_001.pdf">PDF</a>)Movie S1: evolution of perovskite films in water (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.1c01039/suppl_file/nz1c01039_si_002.mp4">MP4</a>)Movie S2: evolution of perovskite films in acetonitrile (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.1c01039/suppl_file/nz1c01039_si_003.mp4">MP4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology,energy & fuels,electrochemistry