Suppression of Atomic Vacancies Via Incorporation of Isovalent Small Ions to Increase the Stability of Halide Perovskite Solar Cells in Ambient Air

Makhsud I. Saidaminov,Junghwan Kim,Ankit Jain,Rafael Quintero-Bermudez,Hairen Tan,Guankui Long,Furui Tan,Andrew Johnston,Yicheng Zhao,Oleksandr Voznyy,Edward H. Sargent

DOI: https://doi.org/10.1038/s41560-018-0192-2

IF: 56.7

2018-01-01

Nature Energy

Abstract:The degradation of perovskite solar cells in the presence of trace water and oxygen poses a challenge for their commercial impact given the appreciable permeability of cost-effective encapsulants. Point defects were recently shown to be a major source of decomposition due to their high affinity for water and oxygen molecules. Here, we report that, in single-cation/halide perovskites, local lattice strain facilitates the formation of vacancies and that cation/halide mixing suppresses their formation via strain relaxation. We then show that judiciously selected dopants can maximize the formation energy of defects responsible for degradation. Cd-containing cells show an order of magnitude enhanced unencapsulated stability compared to state-of-art mixed perovskite solar cells, for both shelf storage and maximum power point operation in ambient air at a relative humidity of 50%. We conclude by testing the generalizability of the defect engineering concept, demonstrating both vacancy-formation suppressors (such as Zn) and promoters (such as Hg).