Abstract:In this study, C/C–SiC and C/C–SiC–ZrC composites were prepared via chemical vapor infiltration and polymer infiltration pyrolysis, and the ablation mechanism under hypersonic oxygen-rich environmental conditions was investigated. The C/C–SiC composites demonstrate an excellent ablation resistance in a hypersonic oxygen-rich environment with a relatively low temperature and speed of approximately 1800 K and 1100 m/s, respectively. It is only in the ablation center area with higher temperatures that a certain degree of thermochemical ablation was observed. The mass and linear ablation rates of C/C–SiC composites (0.027 g/s and 0.117 mm/s, respectively) showed a significant increase in a hypersonic oxygen-rich environment with a temperature and velocity of approximately 2050 K and 2000 m/s, respectively. The high-temperature ablation resistance of ZrC-modified C/C–SiC–ZrC composites improved significantly. However, the ZrC ceramic component had a considerable impact on the ablation resistance of the material. The structural integrity of C/C–20SiC–30ZrC composites was relatively high in hypersonic oxygen-rich environments with a jet temperature and velocity of 2050 K and 2000 m/s, respectively, and mass and linear ablation rates were 0.012 g/s and 0.015 mm/s, respectively. When the ZrC content increased by 40%, the ablation resistance of the composite reduced significantly, whereas the mass and linear ablation rates increased to 0.043 g/s and 0.130 mm/s, respectively.

Effect of loading spectrum with different single pulsing time on the cyclic ablation of C/C-SiC-ZrB2-ZrC composites in plasma

High-frequent pulsing ablation of C/C−SiC−ZrB2−ZrC composite for different cycles to 2000 times in plasma

Effect of Surface Air Cooling on the High Frequent Cyclic Ablation of C/C–SiC–ZrB2–ZrC Composite under Ms-Scale Single Loading

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Cyclic Ablation Properties of C/SiC-ZrC Composites

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Laser ablation behavior and mechanism of Cf/SiC–ZrC ultra-high temperature ceramic matrix composite prepared by PIP method

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Long-term and cyclic ablation behavior of La2O3 modified Cf/ZrB2-SiC composites at 2500 °C

Cyclic Ablation Behaviors of ZrB2–SiC Composites Sintered with Nano‐Sized Particles

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Ablation behavior of sharp leading-edge C/C-ZrC-SiC composites using 3000 C oxyacetylene torch

Ablation mechanism of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC composite during plasma ablation above 2000 °C

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Ablation behavior of C f /ZrC–SiC ultra–high temperature ceramic composites in oxyacetylene torch and plasma wind tunnel

Ceramic Matrix Composite Cyclic Ablation Behavior under Oxyacetylene Torch

The Effects of Laser Parameters and the Ablation Mechanism in Laser Ablation of C/SiC Composite

Study on the Ablation Behavior of C/SiC Composite Materials under the Action of Local Structural Thermal Sources

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Long-term Ablation Behavior of Al4SiC4-YB4 SiC4-YB4 Modified Cf/ZrB2-SiC F /Zrb2-Sic Composites at 2600 °C