Abstract:Due to the randomness of hard and brittle material damage evolution, assessing damage and interpreting mechanisms is challenging. This study focuses on analyzing material damage mechanisms by employing extensive multi-source heterogeneous data to extract quantitative information. A machine vision-based method for detecting and assessing defects in ceramics was proposed, achieving 98 % accuracy. Leveraging this method in scratching experiments, the progression of damage and micro-failure mechanisms in Si3N4 was investigated through the analysis of defect area distribution, force and acoustical signals. Results revealed that the distribution of defect areas conforms to a three-parameter Weibull distribution. At scratch depths of 0.01, 0.02 mm, approximately 90 % of damage accumulated within 1e2–1e4 μm 2 ; conversely, 0.03–0.06 mm led to a decrease to 30 – 40 %. Extensive crack propagation occurs within 0.02–0.03 mm, resulting in the intersecting formation of spalling blocks. Damage evolution occurs in three stages: shallow and small cracks with scattered spalling blocks in the first stage, deep and long cracks with continuous and irregularly shaped spalling blocks in the second stage, and nearly no cracks with continuous and regularly shaped blocks in the third stage. This study not only proposes an efficient method to detect and evaluate ceramic defects, but also deeply understands the evolution process of material damage mechanism. Considering defect distribution and statistical trends, this research not only provide guidance for the optimization of machining parameters, especially in the scene of specific precision and high removal rate. At the same time, the damage evolution and failure mechanism of Si 3 N 4 provide useful experimental basis and data support for deepening the understanding of material behavior during ultra-precision grinding.

The damage mode automatic identification of Al2TiO5 flexible ceramics based on machine learning

Machine learning in Al <sub>2</sub> TiO <sub>5</sub> flexible ceramics with microcrcaks strengthened for damage mode automatic identification

Machine learning in Al<sub>2</sub>TiO<sub>5</sub> flexible ceramics with microcrcaks strengthened for damage mode automatic identification

The influence of sintering temperature on the mechanical evolution of Al2TiO5 flexible ceramics based on the acoustic emission

Method of Damage Characterization of Engineering Ceramics Grinding Surface

Quantification of micro-damage evolution process in ceramics through extensive analysis of multi-source heterogeneous data

Investigation on the microcrcaks strengthening effect in the damage behavior of Al2TiO5 flexible ceramics based on the AE

Damage mode identification of adhesive composite joints under hygrothermal environment using acoustic emission and machine learning

Damage mode effects on fracture strength of ultra-high temperature ceramics

Damage mechanism identification and failure behavior of 2D needle-punched SiC f /SiC composites based on acoustic emission and digital image correlation

Fabrication and Mechanical Properties of Low-Temperature Sintered Al2tio5 Flexible Ceramics

Enhancing the acoustic emission technique using fuzzy artificial bee colony-based deep learning for characterizing selective laser melted AlSi10Mg specimens

Characterizing damage patterns and evolution in Multi-Hole GLARE laminates under tensile load via integrated AE and DIC techniques

Numerical Study of Thermal Shock Damage Mechanism of Polycrystalline Ceramics

Tracing fracture damage evolution and identifying damage patterns in cast steel using advanced acoustic emission analysis

Predicting Fracture Propensity in Amorphous Alumina from Its Static Structure Using Machine Learning

In situ studies on temperature‐dependent deformation mechanisms of Al2O3 prepared by spark plasma sintering

Mechanical Behavior Mechanisms of Al2O3/Al Multilayer Ceramics

Damage and failure analysis of a SiCf/SiC ceramic matrix composite using digital image correlation and acoustic emission

Influence of Cooling Rates on the Microstructure and Mechanical Properties of Aluminum Titanate Flexible Ceramic

In Situ Detection of Damage in the SiC<sub>f</sub>/Ti6242 Composite During the Thermomechanical Fatigue Test