Largely enhanced compressive strength and plastic deformation of Fe-doped all-d-metal heusler alloy Cr 2 CoV

Yunying Li,Yajiu Zhang,Guijiang Li,Zhuhong Liu

DOI: https://doi.org/10.1016/j.intermet.2023.108173

IF: 4.075

2024-01-02

Intermetallics

Abstract:The structure dynamic stability, magnetic property , strength, and plastic deformation of all- d -metal Heusler alloys Cr 2 Co 1- x Fe x V ( x = 0, 0.2, 0.4, 0.6, 0.8, and 1) have been investigated in this study. It is found that Cr 2 Co 1- x Fe x V alloys tend to crystalize in the XA-type Heusler phase. The atomic radius becomes the decisive factor in determining the lattice size. With the increase of Fe concentration, the interaction between Cr(B)-Fe atoms increases, resulting in the increase of Curie temperature. The magnetic moments of the Cr 2 CoV and Cr 2 FeV are analyzed in conjunction with the theoretical calculations. The ductility and compressive strength of the materials gradually increase with the increase of Fe content. Especially in Cr 2 FeV alloy, a high compressive strength of up to 3050 MPa and a large ductility of up to 61% are achieved, and no fracture occurs, showing excellent mechanical properties. The electron localization function diagram shows that d-d orbital hybridization is formed and weak in Cr 2 CoV and Cr 2 FeV alloys, which helps to form metal bonds. Consequently, the ductility of the all- d -metal Heusler alloys was improved, which increased the fatigue life in practical application.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering