Poly(lactic acid) Synthesized from Non‐food Biomass Feedstocks with Tin‐loaded ZA Molecular Sieves Catalysts by Direct Melt Polycondensation

Chengtao Gao,Yanwen Wang,Yunlong Yang,Shuhao Qin

DOI: https://doi.org/10.1002/pi.6594

IF: 3.213

2023-11-22

Polymer International

Abstract:The design and synthesis of catalysts loaded with active components have attracted considerable attention in current research owing to their exceptional catalytic performance. In this study, the focus was on the utilization of tin‐loaded ZA molecular sieves, possessing remarkable adsorption properties, alongside the catalytic activity of tin. These catalysts were successfully prepared and employed for the synthesis of poly(lactic acid) (PLA) from lactic acid (LA) derived from non‐food biomass. By modifying the treatment of ZA molecular sieves, the properties of tin‐loaded ZA molecular sieves were adjusted. The resulting catalysts exhibited a high tin capacity ranging from 2.29% to 2.81% and featured abundant mesoporous structures, providing a surface area of up to 341.2 m2 g–1. Regarding the preparation of PLA, our findings demonstrated that ZA‐III‐Sn2+ as a catalyst yielded PLA with a higher weight‐average molecular weight (Mw) up to 2.57×104 g mol–1 and a higher yield of 65.3% compared to other catalysts. Moreover, the most optimal catalytic effect was achieved by adding the catalyst in three separate stages. Moreover, the amount of catalyst, reaction temperature, and reaction time were found to influence both the molecular weight and yield of PLA. This study not only provides a valuable strategy for the preparation of loaded catalysts for PLA production but also offers new insights into the overall preparation process of PLA. This article is protected by copyright. All rights reserved.

polymer science