High-Efficiency Lithium Metal Anode Enabled by a Concentrated/Fluorinated Ester Electrolyte
Shijian Chen,Yuxuan Xiang,Guorui Zheng,Ying Liao,Fucheng Ren,Yezhen Zheng,Huajin He,Bizhu Zheng,Xiangsi Liu,Ningbo Xu,Mingzeng Luo,Jianming Zheng,Yong Yang
DOI: https://doi.org/10.1021/acsami.0c06930
2020-05-22
Abstract:Lithium (Li) metal anode (LMA) has received growing attention due to its highest theoretical capacity (3860 mA h g<sup>–1</sup>) and lowest redox potential (−3.04 V versus standard hydrogen electrode). However, practical application of LMA is obstructed by the detrimental side reactions between Li metal and organic electrolytes, especially when cycled in traditional carbonate ester electrolytes. Herein, we propose a novel fluorinated carbonate ester-based electrolyte by combining diethyl fluorocarbonate (ETFEC) solvent and 5 M LiFSI concentration (M = mol L<sup>–1</sup>). Using this electrolyte, an ultrahigh Li plating/stripping Coulombic efficiency (CE) of 99.1% can be obtained in Li||Cu cells and a stable cycle performance of Li||LiFePO<sub>4</sub> is achieved under the conditions of limited Li metal (5 mA h cm<sup>–2</sup>), moderate loading LiFePO<sub>4</sub> (7–8 mg cm<sup>–2</sup>), and lean electrolyte (40 uL). The fundamental functioning mechanism of this novel electrolyte has been carefully investigated by scanning electronic microscopy (SEM), operando optical microscopy (OM), electrochemical impedance spectroscopy (EIS), X-ray photoelectron spectroscopy (XPS), and solid state nuclear magnetic resonance (SS-NMR). The results demonstrate that this optimized electrolyte facilitates formation of a high Li<sup>+</sup> conductive SEI layer enriched with LiF and inorganic sulfur-containing species, which can effectively suppress the side reactions between electrolyte and Li metal and prevent formation of dead Li.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c06930?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c06930</a>.Electrochemical cycling performance of Li||Cu cells in different ETFEC-containing electrolytes and different LiFSI concentration electrolytes; electrochemical cycling performance of Li||Cu cells in 5M-DEC electrolyte; EDS mapping images of the SEI formed in 5 M-ETFEC after the 20th Li stripping; X-ray photoelectron spectra of the SEIs formed on Cu substrate in 5 M-DEC electrolyte after 20 cycles; LUMO and HOMO energy values of EC, DEC, ETFEC, and LiFSI; Coulombic efficiency of Li||Cu cells in ester electrolytes reported in the literature (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c06930/suppl_file/am0c06930_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology