Highly concentrated dual-anion electrolyte for non-flammable high-voltage Li-metal batteries

Zhicheng Wang,Yiyang Sun,Yayun Mao,Fengrui Zhang,Lei Zheng,Daosong Fu,Yanbin Shen,Jianchen Hu,Huilong Dong,Jingjing Xu,Xiaodong Wu

DOI: https://doi.org/10.1016/j.ensm.2020.05.020

IF: 20.4

2020-09-01

Energy Storage Materials

Abstract:<p>With a higher demand towards the energy density of power batteries for electric vehicles, the Li-metal batteries (LMBs) have staged a comeback in recent years. However, the low cycle efficiency and safety issues associated with Li dendrite growth and electrolyte combustion severely limit their practical applications. Here we prepare a highly concentrated TFSI-FSI dual-anion electrolyte (HCDE) based on lithium bis(trifluoromethanesulfonyl)imide (LiTFSI), N-ethyl-N-methyl-pyrrolidinium bis(fluorosulfonyl)imide ([C₂mpyr][FSI]), and dimethyl carbonate (DMC). The co-solvent of [C₂mpyr][FSI] and DMC exhibits promoted ionic conductivity, low viscosity and non-flammability. In HCDE, the TFSI-FSI dual-anion is preferentially decomposed to obtain a robust inorganic solid electrolyte interphase (SEI), which induces a dense and uniform Li deposition on the Li-metal surface and effectively suppresses Li dendrite growth. Meanwhile, it also enables good suppression of Al current collector corrosion and stable cycling performance at high-voltage owing to the high salt-to-solvent ratio. The LFP (LiFePO₄)/Li cells steadily deliver a long-term cycle life and obtain ∼80% capacity retention with an extremely high CE (∼99.9%) after 500 cycles, and the NCM523 (LiNi_0.5Co_0.2Mn_0.3O₂)/Li cells retain ∼95% of their original capacity after 100 cycles at a high cut-off voltage of 4.5 V. According to X-ray photoelectron spectroscopy (XPS) and molecular dynamic (MD)-density functional theory (DFT) simulations, the forming mechanism of SEI layer is suggested.</p>

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology