Microstructure and wear resistance of laser cladding NiCrAlY/TC4 composite coatings with in-situ synthesized transition layer by modulating thermal boundary in nitrogen atmosphere

Wenrui Heng,Ming Pang

DOI: https://doi.org/10.1007/s10853-023-09043-9

IF: 4.5

2023-11-03

Journal of Materials Science

Abstract:To improve the wear resistance of TC4 and mitigate surface cracking defects in laser cladding NiCrAlY/TC4 composite coatings, thermal boundary conditions were altered and in-situ generation of enhanced phase transition layers was employed during laser cladding. The microstructure, hardness, and wear behavior were characterized. The results indicated that the TC4/NiCrAlY anti-wear composite coating without cracking defects was manufactured by using insulation layer with the in-situ generation of enhanced phase transition layer technology and has the highest hardness and the best wear resistance. The highest hardness of TC4/NiCrAlY anti-wear composite coating is 653.56 HV 0.5 , which is about twice the hardness of the substrate (350 HV 0.5 ), benefiting from the in-situ synthesis of reinforcing phases such as TiN and Ti 2 AlN. Comparative analysis showed coatings from natural convection, insulation, and in-situ synthesized transition layers possessed mean hardness values of 570.57, 620.91, and 653.56 HV 0.5 , respectively. Enhanced hardness resulted from altered thermal boundary conditions, extending the molten pool's existence, impacting grain size and nitride morphology, etc. Coatings crafted using insulation with in-situ transition layer exhibited minimal wear rates of 2.588 × 10 –4 mm 3 /N m and 0.125 × 10 –4 mm 3 /N m at room temperature and 500 °C. This was due to boundary condition changes fostering dendritic TiN formations, with the finely dispersed reinforced phase exhibiting heightened adherence. Furthermore, the relationship between wear performance and hardness was positively correlated at room temperature but not at 500 °C due to TC4's softening. The coating's wear mechanisms transitioned from abrasive and adhesive wear at room temperature to oxidative wear at 500 °C.

materials science, multidisciplinary