Study on the performance of laser nitriding in situ enhanced Co12/TC4 composite Ag self-lubricating coating on TC4 surface

Zai-Ming Shi,Ming Pang

DOI: https://doi.org/10.1007/s10853-023-09213-9

IF: 4.5

2023-12-12

Journal of Materials Science

Abstract:To enhance the wear resistance of TC4, the fabrication of a TC4/Co12/Ag self-lubricating composite coating was fabricated using laser cladding with N 2 as the protective gas. The resultant composite coating demonstrates a crack-free and defect-free structure. The microstructure, phase composition, and hardness of the composite coatings were analyzed. At the same time, the anti-wear performance of the coating at different temperatures (room temperature (RT), 300 °C, 500 °C) and loads (10 N, 30 N) was systematically investigated. The results show that the in situ generation of TiN and the rapid solidification of the molten pool have an inhibitory effect on the diffusion of Ag. The uniform distribution of Ag with other phases resulted in small fluctuations in hardness. The average hardness reached 597.6 HV 0.5 . The load was increased from 10 to 30 N. The coefficient of friction decreased due to the increase in Ag diffusion. The wear resistance of the coating is superior to the substrate at different conditions, and the minimum wear rate is only 0.005 times of the substrate. The wear rate of the coating increased with increasing temperature at 10N, whereas the opposite trend was observed at 30 N. At RT, the coating experiences abrasive wear caused by Ag. When subjected to a temperature of 300 °C, the coating demonstrates a combination of abrasive and oxidative wear. At 500 °C, the predominant wear mechanism shifts to oxidative wear.

materials science, multidisciplinary