Fast-charging all-solid-state battery cathodes with long cycle life

Christopher Doerrer,Xiangwen Gao,Junfu Bu,Samuel Wheeler,Mauro Pasta,Peter G. Bruce,Patrick S. Grant
DOI: https://doi.org/10.1016/j.nanoen.2024.110531
IF: 17.6
2024-12-02
Nano Energy
Abstract:Many battery applications target fast charging to achieve an 80% rise in state of charge (SOC) in < 15 min. However, in the case of all-solid-state batteries (SSBs), they typically take several hours to reach 80% SOC while retaining a high specific energy of 400 W h kgcell−1 . We specify design strategies for fast-charging SSB cathodes with long cycle life and investigate the fast-charging capability of a sulfide-based single crystal Li- Ni-Mn-Co oxide composite cathode. At 30 °C and charging at 15 mA cm − 2 , a specific capacity of 150 mA h g − 1 was achieved in ∼ 8 min, with 81% capacity retention after 3000 cycles. Critically, a 3-electrode arrangement was used to avoid the common problem of overcharging at high current densities. By following the design strategy and optimized manufacturing, a 210 μm thick cathode was able to be charged at an extraordinary current density of 50 mA cm − 2 to reach an areal capacity of 8 mA h cm − 2 in only 10 min, suggesting practical cathodes for SSBs with 400 W h kgcell−1 may be within reach.
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology
What problem does this paper attempt to address?