Diamond p-type lateral Schottky barrier diodes with high breakdown voltage (4612 V at 0.01 mA/mm)

Zhuoran Han,Can Bayram

DOI: https://doi.org/10.1109/led.2023.3310910

IF: 4.8157

2023-01-01

IEEE Electron Device Letters

Abstract:Diamond p-type lateral Schottky barrier diodes (SBDs) with a 2- $\mu \text{m}$ -thick drift layer are fabricated with and without Al2O3 field plates. Schottky contacts composed of Mo (50 nm) / Pt (50 nm) / Au (100 nm) showed a barrier height of 1.02 ± 0.01 eV and ohmic contacts of Ti (30 nm) / Pt (30 nm) / Au (100 nm) achieved a specific ohmic contact resistance of 1.25 $\pm \,\,0.98\times 10^{-{4}}\,\,\Omega $ -cm2. Their forward and reverse bias characteristics are studied in detail. Both SBDs, with and without Al2O3 field plates, exhibit rectifying ratios larger than 107 at room temperature, and a peak current density of 5.39 mA/mm under 40 V forward bias at 200 °C. The leakage current density at room temperature is stable at approximately 0.01 mA/mm for both diodes. The SBD without the Al2O3 field plate exhibited a breakdown voltage of 1159 V, while the SBD with the Al2O3 field plate is stable under a reverse voltage of 4612 V, which is higher than many diamond SBDs previously reported.

engineering, electrical & electronic