Abstract:This work describes a systematic alloy design strategy resulting in the development of a high strength aluminum alloy adopted for L-PBF. First, based on the composition of a reference Al-Cu-Mg alloy, three Al-Cu-Mg-Mn-Zr-based alloys were investigated using computational thermodynamic tools. Subsequently, the L-PBF processing behavior, microstructure, and concomitant mechanical properties of the L-PBF-fabricated alloys were investigated. Alloys with different compositions showed substantial differences in microstructure: the alloy without Zr addition showed a coarse columnar microstructure and suffered from solidification cracking, alloys with low to mediate Zr additions (1–1.98 wt%) showed a mixed columnar and equiaxed microstructure, while alloys with high Zr addition (3.72 wt%) showed a fully equiaxed microstructure, accompanied by a grain size reduction down to 0.7 ± 0.3 µm. All alloys containing ≥ 1.98 wt% Zr were crack-free. The L-PBF-processed Al-4.40Cu-1.51Mg-1.15Mn-3.72Zr (wt%) alloy showed an extended Zr solid solubility in the Al matrix of ~ 1.3 ± 0.1 wt%. Coherent primary Al3Zr particles with a cubic L12 structure were formed in all the Zr-containing alloys. The mechanical properties of as-built alloys increased consistently with increasing Zr contents from 0 to 3.72 wt%. The designed Al-4.40Cu-1.51Mg-1.15Mn-3.72Zr (wt%) alloy combined a yield strength of 561 ± 24 MPa, an ultimate tensile strength of 580 ± 16 MPa, and an elongation at break of 6.0 ± 1.3%. The exceptionally high strength of this alloy is attributed to a combination of grain refinement, Orowan, solid solution, and dislocation strengthening. The current work shows the intrinsic potential of rapid solidification occurring during L-PBF for the fabrication of geometrically-complex, high-strength lightweight parts made of ultra-fine-grained hyper-peritectic aluminum alloys containing transition element additions.

Preparation of high strength and electrical conductivity copper-chromium pseudobinary alloy by cold-rolling of a billet produced by laser additive manufacturing

Microstructure and mechanical properties of Cu-Cr-Zr alloy prepared by electron beam additive manufacturing and laser-MIG hybrid welding

Performance improvement of laser additive manufactured Cu‒Cr alloy via continuous extrusion

Fabrication of a Strong and Ductile CuCrZr Alloy Using Laser Powder Bed Fusion

High conductive copper alloys for additive manufacturing

Preparation of Cu-Cr-Zr Alloy by Laser Powder Bed Fusion: Parameter Optimization, Microstructure, Mechanical and Thermal Properties for Microelectronic Applications

Laser additive manufacturing of Cu–Cr–Nb alloys by using elemental powder

Effect of cryogenic rolling and multistage thermo-mechanical treatment on the microstructure and properties of the Cu-0.4Cr-0.39Zn-0.1Mg-0.07Zr alloy

Laser–Direct Current arc Hybrid Additive Manufacturing of Cu-Cr-Zr Alloy: Microstructure Evaluation and Mechanical Properties

Effect of heat treatments on microstructure, mechanical and electrical properties of Cu–Cr–Zr alloy manufactured by laser powder bed fusion

Performance Improvement for the CuCrZr Alloy Produced by Laser Powder Bed Fusion Using the Remelting Process

Additive manufacturing of high strength copper alloy with heterogeneous grain structure through laser powder bed fusion

Copper alloys for additive manufacturing: Laser powder bed fusion of CuCr1Zr by using a green qcw-laser

Effect of Process Parameters on the Microstructure and Properties of Cu–Cr–Nb–Ti Alloy Manufactured by Selective Laser Melting

Selective laser melting of Cu–Cr–Zr copper alloy: Parameter optimization, microstructure and mechanical properties

A dual heterogeneous laminated microstructure design for improving the mechanical properties and electrical conductivity of copper alloys

Exceptional Strength Paired with Increased Cold Cracking Susceptibility in Laser Powder Bed Fusion of a Mg-RE Alloy

Achieving superior high-temperature mechanical properties in Al-Cu-Li-Sc-Zr alloy with nano-scale microstructure via laser additive manufacturing

Exploiting the rapid solidification potential of laser powder bed fusion in high strength and crack-free Al-Cu-Mg-Mn-Zr alloys

A promising structure for fabricating high strength and high electrical conductivity copper alloys

Microstructure and mechanical properties of a Cu-1.28Cr-0.24P alloy with high electrical conductivity and tensile strength