Abstract:The effects of temperature on the tribological and dynamic mechanical properties (DMP) of aromatic liquid-crystal poly(ester-co-amide) were investigated. Specimens for the DMA test and friction and wear test were prepared by compression molding at elevated temperature. The dynamic mechanical properties of the resulting compression-molded liquid crystal polymer (LCP) specimens were evaluated on a Perkin-Elmer DMA instrument, in a three-point bending mode, at a heating rate of 10°C/min and frequency of 1Hz from room temperature to 250°C. The friction and wear behavior of the compression-molded LCP specimens sliding against SA52100 steel in a ball-on-disk configuration was evaluated on a high-temperature friction and wear tester from 25 to 300°C. The worn surface morphologies of the compression-molded LCP specimens were observed on a scanning electron microscope. It was found that the tribological and dynamic mechanical properties of the LCP strongly depended on the test temperature. Namely, the friction coefficients decreased significantly and the wear rate increased considerably with increasing temperature. This was attributed to the enhanced softening and plastic deformation of the LCP at elevated temperature. The LCP experienced severe plastic deformation, flowing and local melting owing to the destruction of the stiff backbones of the polymeric molecules at excessively high temperature, thus the largest wear rate of the tested LCP was generated at 300°C. Such a trend in the friction and wear behavior of the compression-molded LCP with temperature conformed well to the corresponding worn surface morphologies. Namely, the LCP worn surface was characterized by mild plastic deformation and micro-cracking as the LCP disk slid against the steel ball at 50°C, whilst at 100°C, the plastic deformation and adhesion became severe and the micro-cracking disappeared owing to the plastic flow. The plastic deformation and adhesion became increasingly more severe with further increase of the test temperature up to 150, 200, and 250°C, owing to the increased plastic flow and local softening and melting of the LCP. Moreover, the storage modulus of the compression-molded LCP greatly decreased with increasing temperature, as did the loss modulus, while the complex modulus and tan δ increased with increasing temperature, which agreed well with the corresponding trend of the tribological behavior with temperature. It was confirmed that the dynamic mechanical properties of the polymer were an important factor of the high temperature tribological behavior.

The influence of temperature on the tribological properties of polyoxymethylene (POM) materials

Effect of Temperature on the Tribological and Dynamic Mechanical Properties of Liquid Crystalline Polymer

A Pin-on-Disk Study of the Tribological Properties of Polyoxymethylene (POM) Gear Materials

Molecular dynamics study on friction of polymer material polyoxymethylene (POM)

Effect of temperature on the tribological properties of Polytetrafluoroethylene/Kevlar fabric/phenolic composites

Investigation on the Tribological Properties of POM Modified by Nano-PTFE

The effects of copper and polytetrafluoroethylene (PTFE) on thermal conductivity and tribological behavior of polyoxymethylene (POM) composites

Effect of temperature on the friction and wear performance of porous oil-containing polyimide

Research on the Tribological Properties of Polyoxymethylene - 40Cr

Thermal Conductivity and Tribological Properties of POM‐Cu Composites

Mechanical and tribological properties of polyoxymethylene modified with nanoparticles and solid lubricants

Effects of thermal‐oxidative aging processes on tribological properties of polyformaldehyde and ultra‐high molecular weight polyethylene : A comparative study

Role of transfer film formation on the tribological properties of polymeric composite materials and spherical plain bearing at low temperatures

Improving the Tribological Performance of POM through the Incorporation of Bio-Based Materials

EFFECT OF THE COMPOUND LUBRICANT SYSTEM ON THE TRIBOLOGICAL PROPERTIES OF POM RESIN

Effect of temperature on friction and wear of polyimide

Modeling of contact temperatures and their influence on the tribological performance of PEEK and PTFE in a dual-pin-on-disk tribometer

Differences in Tribological Behaviors upon Switching Fixed and Moving Materials of Tribo-pairs including Metal and Polymer

Research on the Effect of Temperature on Tribological Properties of PTFE Composites under Oil Lubrication Conditions

Exploring the Friction and Wear Behaviors of Ag-Mo Hybrid Modified Thermosetting Polyimide Composites at High Temperature

Effect of Temperature on Tribological Performances of Molybdenum Dialkyldithiocarbamate