Investigation on high-temperature creep property and mechanism of AA6111 matrix composites reinforced by in-situ ZrB 2 nanoparticles

Wei Qian,Xizhou Kai,Ran Tao,Rui Cao,Chuang Guan,Yutao Zhao

DOI: https://doi.org/10.1016/j.matchar.2022.112620

IF: 4.537

2022-12-29

Materials Characterization

Abstract:In this paper, the AA6111 matrix composites reinforced by in-situ ZrB 2 nanoparticles were fabricated via an Al-Zr-B reaction system and their creep behavior at high temperature was also comprehensively studied. The threshold stress of AA6111-3ZrB 2 composites at 573 K reached to 28 MPa, which was much higher than the only 15 MPa of AA6111 matrix alloy. Besides, the steady state creep rates of AA6111-3ZrB 2 composites were always lower than those of the matrix alloy at the same creep condition, confirming the positive effect on creep property enhancement induced by ZrB 2 particles. The average size of in-situ ZrB 2 particles before and after creep deformation at 573 K/90 MPa was 40 nm and 45 nm respectively, no obvious coarsening phenomenon could be observed. Assisted by the superior thermal stability possessed by ZrB 2 ceramic particles, these nanoparticles could effectively impede dislocation motion and pin grain boundaries during deformation, which was exactly the key reason for such prominent improvement on creep resistance obtained here. In consideration of the presence of creep threshold stress, the true stress exponents of AA6111 alloy and AA6111-3ZrB 2 composites were measured to be 5, indicating the creep mechanism for both of them was dominated by the high-temperature dislocation climbing mechanism.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing